AISI 301 is an austenitic chromium-nickel stainless steel (17-18% Cr, 6-8% Ni) with high work-hardening capacity, used for springs, fasteners, and aerospace components requiring excellent corrosion resistance and moderate strength. Cold-working tempers (1/4 Hard through Full Hard) provide yield strengths from ~200 to 1,200 MPa with retained ductility, while Annealed condition offers lower strength for formability and subsequent hardening.
Compliance & Regulations
2 interactive curves for this material
Stress-strain, S-N fatigue and environmental knockdown curves are free with an account.
Create free account| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Compressive Modulus(Ec)3 entries | Curve (15 pts) | Pa | — | ||
| ↳ | Curve (15 pts) | Pa | — | ||
| ↳ | 193.1 | GPa | 22°C · Sheet/Strip | ||
Poisson's Ratio(ν) | 0.2700 | - | 22°C | ||
Shear Modulus(G) | 77.22 | GPa | 22°C · Sheet/Strip | ||
Young's Modulus(E) | 199.9 | GPa | 22°C · Sheet/Strip |
3 interactive curves for this material
Stress-strain, S-N fatigue and environmental knockdown curves are free with an account.
Create free account| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
CTE vs Temperature(α(T)) | Curve (21 pts) | 1/K | — | ||
Specific Heat vs Temperature(Cp(T)) | Curve (21 pts) | J/(kg·K) | — | ||
Thermal Conductivity vs Temperature(k(T)) | Curve (21 pts) | W/(m·K) | — |
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Density(ρ) | 7.916 | kg/m³ | 22°C |