5083 Aluminum is a non-heat-treatable Al-Mg alloy (approximately 4.4% Mg) with excellent seawater corrosion resistance, used primarily in marine structures, shipbuilding, and chemical storage applications. The O temper is fully annealed, providing maximum ductility and formability with minimum strength, making it suitable for applications requiring extensive cold-working or complex forming operations.
Compliance & Regulations
13 interactive curves for this material
Stress-strain, S-N fatigue and environmental knockdown curves are free with an account.
Create free account| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Ultimate Bearing Strength(Fbru)4 entries | 413.7 | MPa | 22°C · Sheet/Plate · O · AMS 4056 OR AMS-QQ-A-250/6 · t=0.051-1.500 in · e/D=1.5 | ||
| ↳ | 427.5 | MPa | 22°C · Sheet/Plate · O · AMS 4056 OR AMS-QQ-A-250/6 · t=0.051-1.500 in · e/D=1.5 | ||
| ↳ | 524.0 | MPa | 22°C · Sheet/Plate · O · AMS 4056 OR AMS-QQ-A-250/6 · t=0.051-1.500 in · e/D=2 | ||
| ↳ | 537.8 | MPa | 22°C · Sheet/Plate · O · AMS 4056 OR AMS-QQ-A-250/6 · t=0.051-1.500 in · e/D=2 | ||
Bearing Yield Strength(Fbry)4 entries | 220.6 | MPa | 22°C · Sheet/Plate · O · AMS 4056 OR AMS-QQ-A-250/6 · t=0.051-1.500 in · e/D=1.5 | ||
| ↳ | 234.4 | MPa | 22°C · Sheet/Plate · O · AMS 4056 OR AMS-QQ-A-250/6 · t=0.051-1.500 in · e/D=1.5 | ||
| ↳ | 262.0 | MPa | 22°C · Sheet/Plate · O · AMS 4056 OR AMS-QQ-A-250/6 · t=0.051-1.500 in · e/D=2 | ||
| ↳ | 275.8 | MPa | 22°C · Sheet/Plate · O · AMS 4056 OR AMS-QQ-A-250/6 · t=0.051-1.500 in · e/D=2 | ||
Compressive Modulus(Ec) | 71.71 | GPa | 22°C · Sheet/Plate | ||
Compressive Tangent Modulus vs Stress(Etn(σ))4 entries | Curve (11 pts) | Pa | 21°C · L | ||
| ↳ | Curve (11 pts) | Pa | 21°C · LT | ||
| ↳ | Curve (14 pts) | Pa | 21°C · L | ||
| ↳ | Curve (14 pts) | Pa | 21°C · LT | ||
Compressive Yield Strength(Fcy)4 entries | 124.1 | MPa | 22°C · Sheet/Plate · O · AMS 4056 OR AMS-QQ-A-250/6 · L · t=0.051-1.500 in | ||
| ↳ | 131.0 | MPa | 22°C · Sheet/Plate · O · AMS 4056 OR AMS-QQ-A-250/6 · L · t=0.051-1.500 in | ||
| ↳ | 124.1 | MPa | 22°C · Sheet/Plate · O · AMS 4056 OR AMS-QQ-A-250/6 · LT · t=0.051-1.500 in | ||
| ↳ | 131.0 | MPa | 22°C · Sheet/Plate · O · AMS 4056 OR AMS-QQ-A-250/6 · LT · t=0.051-1.500 in | ||
Elongation at Break(εf) | 12.00 – 16.00 | - | 8 entriesClick to expand | ||
Poisson's Ratio(ν) | 0.3300 | - | 22°C | ||
Shear Modulus(G) | 23.10 | GPa | 22°C · Extrusion | ||
Ultimate Shear Strength(Fsu)2 entries | 172.4 | MPa | 22°C · Sheet/Plate · O · AMS 4056 OR AMS-QQ-A-250/6 · t=0.051-1.500 in | ||
| ↳ | 179.3 | MPa | 22°C · Sheet/Plate · O · AMS 4056 OR AMS-QQ-A-250/6 · t=0.051-1.500 in | ||
Stress–Strain Curve(σ–ε) | Curve (16 pts) | Pa | 21°C · L | ||
Stress–Strain Curve (buckling region, ≤ 2% strain)(σ–ε (low-strain)) | — | Pa | 8 entriesClick to expand | ||
Ultimate Tensile Strength(σUTS) | 248.2 – 282.7 | MPa | 10 entriesClick to expand | ||
Yield Strength (0.2% offset)(σy) | 96.53 – 131.0 | MPa | 10 entriesClick to expand | ||
Young's Modulus(E) | 70.33 | GPa | 22°C · Sheet/Plate | ||
2 interactive curves for this material
Stress-strain, S-N fatigue and environmental knockdown curves are free with an account.
Create free account| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
CTE vs Temperature(α(T)) | Curve (9 pts) | 1/K | — | ||
Thermal Conductivity vs Temperature(k(T)) | Curve (20 pts) | W/(m·K) | — |
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Density(ρ) | 2.657 | kg/m³ | 22°C |