Ti-6Al-4V (L-PBF, HIP 926 °C) — Properties & Data | MatWorld

Ti-6Al-4V (L-PBF, HIP 926 °C)

UNS R56400

Ti-6Al-4V made by laser powder bed fusion and then hot isostatically pressed at 926 °C is a printed alpha-beta titanium alloy in its densified condition. As printed, it has fine acicular martensite, columnar prior-beta grains along the build direction, residual stress and some internal pores. Hot isostatic pressing closes internal porosity, relieves residual stress and coarsens the martensite into an alpha-beta structure, improving fatigue performance and ductility at some cost in strength. Surface roughness and surface-connected pores remain, so critical surfaces are usually machined. Parts serve in aerospace structures, medical devices and other fatigue-loaded components.

aerospace structuresmedical devicesfatigue-loaded components

Compliance & Regulations

?UL 94?ITAR?EAR?ISO 10993?Conflict Free?FDA?RoHS?REACH

Ti-6Al-4V (L-PBF)/Ti-6Al-4V (L-PBF, HIP 926 °C)

Units:

si imperial

Property OverviewNormalized to typical max values

1 interactive curve for this material

Stress-strain, S-N fatigue and environmental knockdown curves are free with an account.

Create free account

Filter by

Property	Value	Unit	Conditions
Elongation at Break(εf)	16.70 range 15.90–17.50	%	20°C · specimen ASTM E8, machined after heat treatment · HIP ~926 °C, 100 MPa, 3 h · Z (vertical cylinder
Stress–Strain Curve(σ–ε)	Curve (22 pts)	Pa	20°C · specimen ASTM E8, machined after heat treatment · HIP ~926 °C, 100 MPa, 3 h · Z (vertical cylinder
Ultimate Tensile Strength(σUTS)	1.083 range 1.070–1.096	GPa	20°C · specimen ASTM E8, machined after heat treatment · HIP ~926 °C, 100 MPa, 3 h · Z (vertical cylinder
Yield Strength (0.2% offset)(σy)	1.025 range 1.008–1.042	GPa	20°C · specimen ASTM E8, machined after heat treatment · HIP ~926 °C, 100 MPa, 3 h · Z (vertical cylinder

Verified Unverified Low confidence (<80%) Link to source

Filter by

Property	Value	Unit	Conditions	Source
Density(ρ)	4.410 range 4.404–4.416	kg/m³	20°C · specimen ASTM E8, machined after heat treatment · HIP ~926 °C, 100 MPa, 3 h · Z (vertical cylinder

Verified Unverified Low confidence (<80%) Link to source

Reference data from cited sources. Not verified or certified by MatWorld Inc. Verify against the source before use in design. Terms: engineering data

Regulatory Screening

Environmental

Export Control

Safety & Biocompatibility

Quality & Standards

Industry-Specific

RoHS, REACH, and Prop 65 statuses are validated against official substance lists (ECHA SVHC Candidate List, OEHHA Prop 65, RoHS Annex II). Other regulations are estimated from composition and material classification. All screening is a starting point for due diligence — always verify with your supplier before making compliance decisions.