Inconel 718 (BJT, Desktop Metal Nickel Alloy IN718 (Shop System), HIP) — Properties & Data | MatWorld

Inconel 718 (BJT, Desktop Metal Nickel Alloy IN718 (Shop System), HIP)

UNS N07718· Nickel Alloy IN718 (Shop System)

Desktop Metal Nickel Alloy IN718 (Shop System) in the HIP condition is Inconel 718 printed by metal binder jetting (BJT), sintered and then hot isostatically pressed. Green parts are debound and sintered with substantial shrinkage, giving an equiaxed grain structure without the melt-track texture or residual stress of laser fusion. HIP closes the internal porosity left after sintering, improving ductility and fatigue resistance, though surface-connected pores are not closed. An age-hardening treatment usually follows, and critical surfaces are machined. It is used for complex nickel alloy parts made in batches for high-temperature or corrosive service, such as impellers, nozzles and turbine hardware. Every value on this page is read from Desktop Metal's own material data sheet — quoted, cited and dated — and is the maker's statement about printed material, not a measurement by MatWorld; none has yet been reviewed by a person.

impellersnozzlesturbine hardware

Compliance & Regulations

?UL 94?ITAR?EAR?ISO 10993?Conflict Free?FDA?RoHS?REACH

Inconel 718 (BJT)/Inconel 718 (BJT, Desktop Metal Nickel Alloy IN718 (Shop System), HIP)

Units:

si imperial

Property OverviewNormalized to typical max values

Filter by

Table

Orientation

Specification

Property	Value	Unit	Conditions
Elongation at Break(εf)3 entries	12.80 range 11.40–14.20	%	MECHANICAL PROPERTIES IN DESKTOP METAL PURESINTER FURNACE · HIP · ASTM E8/E8M · X
↳	11.20 range 8.200–14.20	%	Sintered in an Elnik MIM 3000 series metal hot zone furnace and tested in the as printed surface con · HIP · ASTM E8/E21 · XY
↳	16.00 range 13.00–19.00	%	Sintered in an Elnik MIM 3000 series metal hot zone furnace and tested in the machined surface condi · HIP · ASTM E8/E21 · XY
Hardness (Rockwell C)(HRC)2 entries	43.10 range 42.40–43.80	HRC	MECHANICAL PROPERTIES IN DESKTOP METAL PURESINTER FURNACE · HIP · ASTM E18 · X
↳	43.00 range 42.00–44.00	HRC	Sintered in an Elnik MIM 3000 series metal hot zone furnace and tested in the as printed surface con · HIP · ASTM E18 · XY
Reduction of Area(RA)3 entries	13.90 range 12.30–15.50	%	MECHANICAL PROPERTIES IN DESKTOP METAL PURESINTER FURNACE · HIP · ASTM E8/E8M · X
↳	13.70 range 11.70–15.70	%	Sintered in an Elnik MIM 3000 series metal hot zone furnace and tested in the as printed surface con · HIP · ASTM E8/E21 · XY
↳	19.00 range 16.00–22.00	%	Sintered in an Elnik MIM 3000 series metal hot zone furnace and tested in the machined surface condi · HIP · ASTM E8/E21 · XY
Ultimate Tensile Strength(σUTS)3 entries	1.270 range 1.259–1.281	GPa	MECHANICAL PROPERTIES IN DESKTOP METAL PURESINTER FURNACE · HIP · ASTM E8/E8M · X
↳	1.267 range 1.242–1.292	GPa	Sintered in an Elnik MIM 3000 series metal hot zone furnace and tested in the as printed surface con · HIP · ASTM E8/E21 · XY
↳	1.051 range 1.045–1.057	GPa	Sintered in an Elnik MIM 3000 series metal hot zone furnace and tested in the machined surface condi · HIP · ASTM E8/E21 · XY
Yield Strength (0.2% offset)(σy)3 entries	1.080 range 1.067–1.093	GPa	MECHANICAL PROPERTIES IN DESKTOP METAL PURESINTER FURNACE · HIP · ASTM E8/E8M · X
↳	1.055 range 1.033–1.077	GPa	Sintered in an Elnik MIM 3000 series metal hot zone furnace and tested in the as printed surface con · HIP · ASTM E8/E21 · XY
↳	908.0 range 899.0–917.0	MPa	Sintered in an Elnik MIM 3000 series metal hot zone furnace and tested in the machined surface condi · HIP · ASTM E8/E21 · XY
Young's Modulus(E)2 entries	205.0	GPa	MECHANICAL PROPERTIES IN DESKTOP METAL PURESINTER FURNACE · HIP · ASTM E111 · X
↳	187.0	GPa	Sintered in an Elnik MIM 3000 series metal hot zone furnace and tested in the as printed surface con · HIP · ASTM E111 · XY

N entriesMultiple entries per property — large groups are collapsed; click a summary row to expand. Use filters above to narrow by form, heat treatment, basis, or test environment.

Verified Unverified Low confidence (<80%) Link to source

Filter by

Statistic

Table

Property	Value	Unit	Conditions	Source
Density(ρ)2 entries	8.229 range 8.227–8.231	kg/m³	MECHANICAL PROPERTIES IN DESKTOP METAL PURESINTER FURNACE · HIP · ASTM B311
↳	8.200	kg/m³	Sintered in an Elnik MIM 3000 series metal hot zone furnace and tested in the as printed surface con · HIP · ASTM B311

N entriesMultiple entries per property — large groups are collapsed; click a summary row to expand. Use filters above to narrow by form, heat treatment, basis, or test environment.

Verified Unverified Low confidence (<80%) Link to source

Reference data from cited sources. Not verified or certified by MatWorld Inc. Verify against the source before use in design. Terms: engineering data

Regulatory Screening

Environmental

Export Control

Safety & Biocompatibility

Quality & Standards

Industry-Specific

RoHS, REACH, and Prop 65 statuses are validated against official substance lists (ECHA SVHC Candidate List, OEHHA Prop 65, RoHS Annex II). Other regulations are estimated from composition and material classification. All screening is a starting point for due diligence — always verify with your supplier before making compliance decisions.