Custom 455 is a precipitation-hardening martensitic stainless steel (Fe-Ni-Cr-Mo-Ti base) used primarily in aerospace applications requiring high strength at elevated temperatures up to 1000°F. The H1000 condition provides peak hardness and strength through aging treatment, delivering ultimate tensile strength around 180–200 ksi with good fatigue and bearing load characteristics, making it suitable for critical rotating components and fasteners in gas turbine engines and launch vehicle structures.
Compliance & Regulations
10 interactive curves for this material
Stress-strain, S-N fatigue and environmental knockdown curves are free with an account.
Create free account| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Ultimate Bearing Strength(Fbru)2 entries | 2.234 | GPa | 22°C · Bar · H1000 · AMS 5617 · t=≤8.000 in · e/D=1.5 | ||
| ↳ | 2.820 | GPa | 22°C · Bar · H1000 · AMS 5617 · t=≤8.000 in · e/D=2 | ||
Bearing Yield Strength(Fbry)2 entries | 1.965 | GPa | 22°C · Bar · H1000 · AMS 5617 · t=≤8.000 in · e/D=1.5 | ||
| ↳ | 2.365 | GPa | 22°C · Bar · H1000 · AMS 5617 · t=≤8.000 in · e/D=2 | ||
Compressive Modulus(Ec) | 206.8 | GPa | 22°C · Tubing (Welded) | ||
Compressive Yield Strength(Fcy)3 entries | 1.331 | GPa | 22°C · Bar · H1000 · AMS 5617 · L · t=≤8.000 in | ||
| ↳ | 1.331 | GPa | 22°C · Bar · H1000 · AMS 5617 · LT · t=≤8.000 in | ||
| ↳ | 1.331 | GPa | 22°C · Bar · H1000 · AMS 5617 · ST · t=≤8.000 in | ||
Elongation at Break(εf)2 entries | 10.00 | - | 22°C · Bar · H1000 · AMS 5617 · L · t=≤8.000 in | ||
| ↳ | Curve (13 pts) | - | L | ||
Poisson's Ratio(ν) | 0.2700 | - | 22°C | ||
Reduction of Area(RA) | 40.00 | - | 22°C · Bar · H1000 · AMS 5617 · L · t=≤8.000 in | ||
Reduction of Area vs Temperature(RA(T)) | Curve (14 pts) | - | L | ||
Shear Modulus(G) | 77.91 | GPa | 22°C · Tubing (Welded) | ||
Ultimate Shear Strength(Fsu)2 entries | 854.9 | MPa | 22°C · Bar · H1000 · AMS 5617 · t=≤8.000 in | ||
| ↳ | Curve (10 pts) | Pa | — | ||
S–N Curve (Wöhler)(S–N)3 entries | Curve (40 pts) | Pa | 21°C · L | ||
| ↳ | Curve (40 pts) | Pa | 21°C · L | ||
| ↳ | Curve (40 pts) | Pa | 21°C · L | ||
Stress–Strain Curve (buckling region, ≤ 2% strain)(σ–ε (low-strain))2 entries | Curve (8 pts) | Pa | 21°C · L | ||
| ↳ | Curve (8 pts) | Pa | 21°C · LT | ||
Ultimate Tensile Strength(σUTS)2 entries | 1.379 | GPa | 22°C · Bar · H1000 · AMS 5617 · L · t=≤8.000 in | ||
| ↳ | Curve (8 pts) | Pa | L | ||
Yield Strength (0.2% offset)(σy)2 entries | 1.276 | GPa | 22°C · Bar · H1000 · AMS 5617 · L · t=≤8.000 in | ||
| ↳ | Curve (9 pts) | Pa | L | ||
Young's Modulus(E) | 196.5 | GPa | 22°C · Tubing (Welded) |
2 interactive curves for this material
Stress-strain, S-N fatigue and environmental knockdown curves are free with an account.
Create free account| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
CTE vs Temperature(α(T)) | Curve (9 pts) | 1/K | — | ||
Thermal Conductivity vs Temperature(k(T)) | Curve (9 pts) | W/(m·K) | — |
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Density(ρ) | 7.750 | kg/m³ | 22°C |