Custom 455 Stainless Steel H1000
VerifiedmetalCustom 455 is a precipitation-hardening martensitic stainless steel (Fe-Ni-Cr-Mo-Ti base) used primarily in aerospace applications requiring high strength at elevated temperatures up to 1000°F. The H1000 condition provides peak hardness and strength through aging treatment, delivering ultimate tensile strength around 180–200 ksi with good fatigue and bearing load characteristics, making it suitable for critical rotating components and fasteners in gas turbine engines and launch vehicle structures.
aerospacestructural
Compliance & Regulations
?Conflict Free?RoHS?REACH?TSCA?Prop 65
Property OverviewNormalized to typical max values
Filter by
Form
e/D Ratio
Orientation
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Ultimate Bearing Strength(Fbru)2 entries | 324 | ksi | 22°C · Bar · H1000 · AMS 5617 · t=≤8.000 in · e/D=1.5 | ||
| ↳ | 409 | ksi | 22°C · Bar · H1000 · AMS 5617 · t=≤8.000 in · e/D=2 | ||
Bearing Yield Strength(Fbry)2 entries | 285 | ksi | 22°C · Bar · H1000 · AMS 5617 · t=≤8.000 in · e/D=1.5 | ||
| ↳ | 343 | ksi | 22°C · Bar · H1000 · AMS 5617 · t=≤8.000 in · e/D=2 | ||
Compressive Modulus(Ec) | 30,000 | ksi | 22°C · Tubing (Welded) | ||
Compressive Yield Strength(Fcy)3 entries | 193 | ksi | 22°C · Bar · H1000 · AMS 5617 · L · t=≤8.000 in | ||
| ↳ | 193 | ksi | 22°C · Bar · H1000 · AMS 5617 · LT · t=≤8.000 in | ||
| ↳ | 193 | ksi | 22°C · Bar · H1000 · AMS 5617 · ST · t=≤8.000 in | ||
Elongation at Break(εf)2 entries | 10.00 | - | 22°C · Bar · H1000 · AMS 5617 · L · t=≤8.000 in | ||
| ↳ | Curve (13 pts) | - | L | ||
Poisson's Ratio(ν) | 0.2700 | - | 22°C | ||
Reduction of Area(RA) | 40.00 | - | 22°C · Bar · H1000 · AMS 5617 · L · t=≤8.000 in | ||
Reduction of Area vs Temperature(RA(T)) | Curve (14 pts) | - | L | ||
Shear Modulus(G) | 11,300 | ksi | 22°C · Tubing (Welded) | ||
Ultimate Shear Strength(Fsu)2 entries | 124 | ksi | 22°C · Bar · H1000 · AMS 5617 · t=≤8.000 in | ||
| ↳ | Curve (10 pts) | ksi | — | ||
S–N Curve (Wöhler)(S–N)3 entries | Curve (40 pts) | ksi | 21°C · L | ||
| ↳ | Curve (40 pts) | ksi | 21°C · L | ||
| ↳ | Curve (40 pts) | ksi | 21°C · L | ||
Stress–Strain Curve (buckling region, ≤ 2% strain)(σ–ε (low-strain))2 entries | Curve (8 pts) | ksi | 21°C · L | ||
| ↳ | Curve (8 pts) | ksi | 21°C · LT | ||
Ultimate Tensile Strength(σUTS)2 entries | 200 | ksi | 22°C · Bar · H1000 · AMS 5617 · L · t=≤8.000 in | ||
| ↳ | Curve (8 pts) | ksi | L | ||
Yield Strength (0.2% offset)(σy)2 entries | 185 | ksi | 22°C · Bar · H1000 · AMS 5617 · L · t=≤8.000 in | ||
| ↳ | Curve (9 pts) | ksi | L | ||
Young's Modulus(E) | 28,500 | ksi | 22°C · Tubing (Welded) |
N entriesMultiple entries per property — large groups are collapsed; click a summary row to expand. Use filters above to narrow by form / heat treatment / basis.
Rows with are inherited from the base material
Verified Unverified Low confidence (<80%) Link to source
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
CTE vs Temperature(α(T)) | Curve (9 pts) | µin/in·°F | — | ||
Thermal Conductivity vs Temperature(k(T)) | Curve (9 pts) | BTU/(hr·ft·°F) | — |
Rows with are inherited from the base material
Verified Unverified Low confidence (<80%) Link to source
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Density(ρ) | 0.2800 | lb/in³ | 22°C |
Rows with are inherited from the base material
Verified Unverified Low confidence (<80%) Link to source
Regulatory Screening
Environmental
Quality & Standards
Industry-Specific
RoHS, REACH, and Prop 65 statuses are validated against official substance lists (ECHA SVHC Candidate List, OEHHA Prop 65, RoHS Annex II). Other regulations are estimated from composition and material classification. All screening is a starting point for due diligence — always verify with your supplier before making compliance decisions.