Engineered laminate of AW280-5H/3501-6, stacked [(0/45/90/-45):f]:s. Properties here are laminate-level effective values in the laminate's own axes — not the lamina constants, which live on the parent prepreg (AW280-5H/3501-6 — AS4 carbon/3501-6). From MIL-HDBK-17-2F Volume 2 (US Government work, public domain).
Compliance & Regulations
Fiber Direction
Ply Schedule
Laminate Code
[0/45/90/-45/-45/90/45/0]s
Fiber angles relative to the 0° reference direction (red arrow in 3D view). 0° = longitudinal, 90° = transverse, ±45° = shear paths.
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Compressive Modulus(Ec) | 59.98 range 52.40–64.81n=13, 3 batches, CV 8.2% | GPa | 24°C · RTA · 1-axis · [0:f]:8 · norm. thk+Vf | ||
Compressive Strength(σc) | 730.8 range 627.4–792.9n=13, 3 batches, CV 6.52% | MPa | 24°C · RTA · 1-axis · [0:f]:8 · norm. thk+Vf | ||
Interlaminar Shear Strength(ILSS) | 68.46 range 58.61–73.77n=9, 3 batches, CV 7.38% | MPa | 24°C · RTA · 13-axis · [0]:15 · as-measured | ||
Ultimate Tensile Strength(σUTS)2 entries | 554.3 range 531.6–595.7n=9, 3 batches, CV 3.85% | MPa | 24°C · RTA · x-axis · [(0/45/90/-45):f]:s · norm. thk+Vf | ||
| ↳ | 519.2 range 474.4–565.4n=9, 3 batches, CV 5.41% | MPa | 24°C · RTA · x-axis · [(0/45/90/-45):f]:s · as-measured | ||
Young's Modulus(E)2 entries | 47.85 range 46.40–49.16n=9, 3 batches, CV 1.87% | GPa | 24°C · RTA · x-axis · [(0/45/90/-45):f]:s · norm. thk+Vf | ||
| ↳ | 44.82 range 43.44–45.51n=9, 3 batches, CV 2.04% | GPa | 24°C · RTA · x-axis · [(0/45/90/-45):f]:s · as-measured |