Engineered laminate of AW280-5H/3501-6, stacked [(0/45/90/-45):f]:s. Properties here are laminate-level effective values in the laminate's own axes — not the lamina constants, which live on the parent prepreg (AW280-5H/3501-6 — AS4 carbon/3501-6). From MIL-HDBK-17-2F Volume 2 (US Government work, public domain).
Compliance & Regulations
Fiber Direction
Ply Schedule
Laminate Code
[0/45/90/-45/-45/90/45/0]s
Fiber angles relative to the 0° reference direction (red arrow in 3D view). 0° = longitudinal, 90° = transverse, ±45° = shear paths.
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Compressive Modulus(Ec) | 8,700 range 7,600–9,400n=13, 3 batches, CV 8.2% | ksi | 24°C · RTA · 1-axis · [0:f]:8 · norm. thk+Vf | ||
Compressive Strength(σc) | 106 range 91.00–115n=13, 3 batches, CV 6.52% | ksi | 24°C · RTA · 1-axis · [0:f]:8 · norm. thk+Vf | ||
Interlaminar Shear Strength(ILSS) | 9.930 range 8.500–10.70n=9, 3 batches, CV 7.38% | ksi | 24°C · RTA · 13-axis · [0]:15 · as-measured | ||
Ultimate Tensile Strength(σUTS)2 entries | 80.40 range 77.10–86.40n=9, 3 batches, CV 3.85% | ksi | 24°C · RTA · x-axis · [(0/45/90/-45):f]:s · norm. thk+Vf | ||
| ↳ | 75.30 range 68.80–82.00n=9, 3 batches, CV 5.41% | ksi | 24°C · RTA · x-axis · [(0/45/90/-45):f]:s · as-measured | ||
Young's Modulus(E)2 entries | 6,940 range 6,730–7,130n=9, 3 batches, CV 1.87% | ksi | 24°C · RTA · x-axis · [(0/45/90/-45):f]:s · norm. thk+Vf | ||
| ↳ | 6,500 range 6,300–6,600n=9, 3 batches, CV 2.04% | ksi | 24°C · RTA · x-axis · [(0/45/90/-45):f]:s · as-measured |