6061 Aluminum T42
VerifiedmetalUNS A96061
6061 Aluminum T42 is a precipitation-hardened aluminum-magnesium-silicon alloy in a solution heat-treated and artificially aged condition, providing moderate strength with good corrosion resistance and weldability suitable for aerospace structural applications. Available in rolled, drawn, or cold-finished rod and special shapes per AMS-QQ-A-225/8, this temper balances tensile strength, yield strength, and ductility for applications requiring reliable performance at moderate temperatures.
aerospacestructural
Compliance & Regulations
?Conflict Free?FDA?RoHS?REACH?TSCA?Prop 65
Filter by
Form
Thickness
Specification
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Compressive Modulus(Ec) | — | Pa | 22°C · Rolled, drawn, or cold-finished rod and special shapes | — | |
Elongation at Break(εf)2 entries | — | - | 22°C · Rolled, drawn, or cold-finished rod and special shapes · T42a · AMS-QQ-A-225/8 · L · t=≤8.000 in | — | |
| ↳ | — | - | 22°C · Bar/Extrusion/Rod · T42a · AMS-QQ-A-200/8 · L · t=All in | — | |
Poisson's Ratio(ν) | — | - | 22°C | — | |
Shear Modulus(G) | — | Pa | 22°C · Rolled, drawn, or cold-finished rod and special shapes | — | |
Ultimate Tensile Strength(σUTS)2 entries | — | Pa | 22°C · Rolled, drawn, or cold-finished rod and special shapes · T42a · AMS-QQ-A-225/8 · L · t=≤8.000 in | — | |
| ↳ | — | Pa | 22°C · Bar/Extrusion/Rod · T42a · AMS-QQ-A-200/8 · L · t=All in | — | |
Yield Strength (0.2% offset)(σy)2 entries | — | Pa | 22°C · Rolled, drawn, or cold-finished rod and special shapes · T42a · AMS-QQ-A-225/8 · L · t=≤8.000 in | — | |
| ↳ | — | Pa | 22°C · Bar/Extrusion/Rod · T42a · AMS-QQ-A-200/8 · L · t=All in | — | |
Young's Modulus(E) | — | Pa | 22°C · Rolled, drawn, or cold-finished rod and special shapes | — |
N entriesMultiple entries per property — large groups are collapsed; click a summary row to expand. Use filters above to narrow by form / heat treatment / basis.
Rows with are inherited from the base material
Verified Unverified Low confidence (<80%) Link to source
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
CTE vs Temperature(α(T)) | Curve (11 pts) | 1/K | — | — | |
Specific Heat vs Temperature(Cp(T)) | Curve (17 pts) | J/(kg·K) | — | — |
Verified Unverified Low confidence (<80%) Link to source
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Density(ρ) | — | kg/m³ | 22°C | — |
Rows with are inherited from the base material
Verified Unverified Low confidence (<80%) Link to source
Regulatory Screening
Environmental
Safety & Biocompatibility
Quality & Standards
Industry-Specific
RoHS, REACH, and Prop 65 statuses are validated against official substance lists (ECHA SVHC Candidate List, OEHHA Prop 65, RoHS Annex II). Other regulations are estimated from composition and material classification. All screening is a starting point for due diligence — always verify with your supplier before making compliance decisions.