5086 Aluminum H36
Verifiedmetal5086-H36 is a non-heat-treatable aluminum-magnesium alloy (approximately 3-4% Mg) commonly used in marine, pressure vessel, and aerospace applications requiring superior seawater corrosion resistance and weldability. The H36 temper (strain-hardened and partially annealed) provides moderate strength with enhanced formability compared to fully hard conditions, making it suitable for structural applications in sheet and plate form where both strength and corrosion resistance are critical.
aerospacestructural
Compliance & Regulations
?Conflict Free?FDA?RoHS?REACH?TSCA?Prop 65
Filter by
Form
e/D Ratio
Orientation
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Ultimate Bearing Strength(Fbru)2 entries | — | Pa | 22°C · Sheet/Plate · H36 · AMS-QQ-A-250/7 · t=0.006-0.162 in · e/D=1.5 | — | |
| ↳ | — | Pa | 22°C · Sheet/Plate · H36 · AMS-QQ-A-250/7 · t=0.006-0.162 in · e/D=2 | — | |
Bearing Yield Strength(Fbry) | — | Pa | 22°C · Sheet/Plate · H36 · AMS-QQ-A-250/7 · t=0.006-0.162 in · e/D=1.5 | — | |
Compressive Modulus(Ec) | — | Pa | 22°C · Sheet/Plate | — | |
Compressive Tangent Modulus vs Stress(Etn(σ))2 entries | Curve (11 pts) | Pa | 21°C · L | — | |
| ↳ | Curve (13 pts) | Pa | 21°C · LT | — | |
Compressive Yield Strength(Fcy)3 entries | — | Pa | 22°C · Sheet/Plate · H36 · AMS-QQ-A-250/7 · L · t=0.006-0.162 in | — | |
| ↳ | — | Pa | 22°C · Sheet/Plate · H36 · AMS-QQ-A-250/7 · LT · t=0.006-0.162 in | — | |
| ↳ | — | Pa | 22°C · Sheet/Plate · H36 · AMS-QQ-A-250/7 · ST · t=0.006-0.162 in | — | |
Poisson's Ratio(ν) | — | - | 22°C | — | |
Shear Modulus(G) | — | Pa | 22°C · Sheet/Plate | — | |
Ultimate Shear Strength(Fsu) | — | Pa | 22°C · Sheet/Plate · H36 · AMS-QQ-A-250/7 · t=0.006-0.162 in | — | |
Stress–Strain Curve (buckling region, ≤ 2% strain)(σ–ε (low-strain))4 entries | Curve (8 pts) | Pa | 21°C · L | — | |
| ↳ | Curve (11 pts) | Pa | 21°C · L | — | |
| ↳ | Curve (13 pts) | Pa | 21°C · LT | — | |
| ↳ | Curve (9 pts) | Pa | 21°C · LT | — | |
Ultimate Tensile Strength(σUTS)2 entries | — | Pa | 22°C · Sheet/Plate · H36 · AMS-QQ-A-250/7 · L · t=0.006-0.162 in | — | |
| ↳ | — | Pa | 22°C · Sheet/Plate · H36 · AMS-QQ-A-250/7 · LT · t=0.006-0.162 in | — | |
Yield Strength (0.2% offset)(σy)2 entries | — | Pa | 22°C · Sheet/Plate · H36 · AMS-QQ-A-250/7 · L · t=0.006-0.162 in | — | |
| ↳ | — | Pa | 22°C · Sheet/Plate · H36 · AMS-QQ-A-250/7 · LT · t=0.006-0.162 in | — | |
Young's Modulus(E) | — | Pa | 22°C · Sheet/Plate | — |
N entriesMultiple entries per property — large groups are collapsed; click a summary row to expand. Use filters above to narrow by form / heat treatment / basis.
Rows with are inherited from the base material
Verified Unverified Low confidence (<80%) Link to source
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
CTE vs Temperature(α(T)) | Curve (17 pts) | 1/K | — | — | |
Thermal Conductivity vs Temperature(k(T)) | Curve (20 pts) | W/(m·K) | — | — |
Rows with are inherited from the base material
Verified Unverified Low confidence (<80%) Link to source
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Density(ρ) | — | kg/m³ | 22°C | — |
Rows with are inherited from the base material
Verified Unverified Low confidence (<80%) Link to source
Regulatory Screening
Environmental
Safety & Biocompatibility
Quality & Standards
Industry-Specific
RoHS, REACH, and Prop 65 statuses are validated against official substance lists (ECHA SVHC Candidate List, OEHHA Prop 65, RoHS Annex II). Other regulations are estimated from composition and material classification. All screening is a starting point for due diligence — always verify with your supplier before making compliance decisions.