ZK60A F
VerifiedmetalZK60A-F is a magnesium alloy containing zinc and zirconium, used in aerospace applications requiring lightweight structural components with moderate strength and operating temperatures up to approximately 150°C; the F (as-fabricated) temper represents the material in its extruded condition without heat treatment, providing consistent properties suitable for cast and wrought magnesium applications per ASTM B 107.
aerospacestructural
Compliance & Regulations
?EAR?Conflict Free?RoHS?REACH?TSCA?Prop 65
Property OverviewNormalized to typical max values
Filter by
Form
Thickness
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Ultimate Bearing Strength(Fbru) | 70.00 | ksi | 22°C · Bar/Extrusion/Rod · F · ASTM B 107 · t=All in · e/D=2 | ||
Bearing Yield Strength(Fbry) | 45.00 | ksi | 22°C · Bar/Extrusion/Rod · F · ASTM B 107 · t=All in · e/D=2 | ||
Compressive Modulus(Ec) | 6,500 | ksi | 22°C · Bar/Extrusion/Rod | ||
Compressive Yield Strength(Fcy)3 entries | 20.00 | ksi | 22°C · Extrusion/Tubing · F · ASTM B 107 · L · t=0.028-0.750 wall in | ||
| ↳ | 27.00 | ksi | 22°C · Bar/Extrusion/Rod · F · ASTM B 107 · L · t=All in | ||
| ↳ | 20.00 | ksi | 22°C · Extruded hollow shapes · F · ASTM B 107 · L · t=All in | ||
Elongation at Break(εf)3 entries | 5.000 | - | 22°C · Bar/Extrusion/Rod · F · ASTM B 107 · L · t=All in | ||
| ↳ | 5.000 | - | 22°C · Extruded hollow shapes · F · ASTM B 107 · L · t=All in | ||
| ↳ | 5.000 | - | 22°C · Extrusion/Tubing · F · ASTM B 107 · L · t=0.028-0.750 wall in | ||
Poisson's Ratio(ν) | 0.3500 | - | 22°C | ||
Shear Modulus(G) | 2,400 | ksi | 22°C · Bar/Extrusion/Rod | ||
Ultimate Shear Strength(Fsu) | 22.00 | ksi | 22°C · Bar/Extrusion/Rod · F · ASTM B 107 · t=All in | ||
S–N Curve (Wöhler)(S–N) | Curve (40 pts) | ksi | 21°C · L | ||
Stress–Strain Curve (buckling region, ≤ 2% strain)(σ–ε (low-strain)) | Curve (13 pts) | ksi | 21°C · L | ||
Ultimate Tensile Strength(σUTS)3 entries | 43.00 | ksi | 22°C · Bar/Extrusion/Rod · F · ASTM B 107 · L · t=All in | ||
| ↳ | 40.00 | ksi | 22°C · Extruded hollow shapes · F · ASTM B 107 · L · t=All in | ||
| ↳ | 40.00 | ksi | 22°C · Extrusion/Tubing · F · ASTM B 107 · L · t=0.028-0.750 wall in | ||
Yield Strength (0.2% offset)(σy)3 entries | 31.00 | ksi | 22°C · Bar/Extrusion/Rod · F · ASTM B 107 · L · t=All in | ||
| ↳ | 28.00 | ksi | 22°C · Extruded hollow shapes · F · ASTM B 107 · L · t=All in | ||
| ↳ | 28.00 | ksi | 22°C · Extrusion/Tubing · F · ASTM B 107 · L · t=0.028-0.750 wall in | ||
Young's Modulus(E) | 6,500 | ksi | 22°C · Bar/Extrusion/Rod |
N entriesMultiple entries per property — large groups are collapsed; click a summary row to expand. Use filters above to narrow by form / heat treatment / basis.
Rows with are inherited from the base material
Verified Unverified Low confidence (<80%) Link to source
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Thermal Conductivity vs Temperature(k(T)) | Curve (4 pts) | BTU/(hr·ft·°F) | — |
Rows with are inherited from the base material
Verified Unverified Low confidence (<80%) Link to source
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Density(ρ) | 0.06590 | lb/in³ | 22°C |
Rows with are inherited from the base material
Verified Unverified Low confidence (<80%) Link to source
Regulatory Screening
Environmental
Export Control
RoHS, REACH, and Prop 65 statuses are validated against official substance lists (ECHA SVHC Candidate List, OEHHA Prop 65, RoHS Annex II). Other regulations are estimated from composition and material classification. All screening is a starting point for due diligence — always verify with your supplier before making compliance decisions.