ZK60A F

Verifiedmetal

ZK60A-F is a magnesium alloy containing zinc and zirconium, used in aerospace applications requiring lightweight structural components with moderate strength and operating temperatures up to approximately 150°C; the F (as-fabricated) temper represents the material in its extruded condition without heat treatment, providing consistent properties suitable for cast and wrought magnesium applications per ASTM B 107.

aerospacestructural

Compliance & Regulations

?EAR?Conflict Free?RoHS?REACH?TSCA?Prop 65

ZK60A/ZK60A F

Units:

si imperial

Property OverviewNormalized to typical max values

2 interactive curves for this material

Stress-strain, S-N fatigue and environmental knockdown curves are free with an account.

Create free account

Filter by

Form

Thickness

Property	Value	Unit	Conditions
Ultimate Bearing Strength(Fbru)	482.6	MPa	22°C · Bar/Extrusion/Rod · F · ASTM B 107 · t=All in · e/D=2
Bearing Yield Strength(Fbry)	310.3	MPa	22°C · Bar/Extrusion/Rod · F · ASTM B 107 · t=All in · e/D=2
Compressive Modulus(Ec)	44.82	GPa	22°C · Bar/Extrusion/Rod
Compressive Yield Strength(Fcy)3 entries	137.9	MPa	22°C · Extrusion/Tubing · F · ASTM B 107 · L · t=0.028-0.750 wall in
↳	186.2	MPa	22°C · Bar/Extrusion/Rod · F · ASTM B 107 · L · t=All in
↳	137.9	MPa	22°C · Extruded hollow shapes · F · ASTM B 107 · L · t=All in
Elongation at Break(εf)3 entries	5.000	-	22°C · Bar/Extrusion/Rod · F · ASTM B 107 · L · t=All in
↳	5.000	-	22°C · Extruded hollow shapes · F · ASTM B 107 · L · t=All in
↳	5.000	-	22°C · Extrusion/Tubing · F · ASTM B 107 · L · t=0.028-0.750 wall in
Poisson's Ratio(ν)	0.3500	-	22°C
Shear Modulus(G)	16.55	GPa	22°C · Bar/Extrusion/Rod
Ultimate Shear Strength(Fsu)	151.7	MPa	22°C · Bar/Extrusion/Rod · F · ASTM B 107 · t=All in
S–N Curve (Wöhler)(S–N)	Curve (40 pts)	Pa	21°C · L
Stress–Strain Curve (buckling region, ≤ 2% strain)(σ–ε (low-strain))	Curve (13 pts)	Pa	21°C · L
Ultimate Tensile Strength(σUTS)3 entries	296.5	MPa	22°C · Bar/Extrusion/Rod · F · ASTM B 107 · L · t=All in
↳	275.8	MPa	22°C · Extruded hollow shapes · F · ASTM B 107 · L · t=All in
↳	275.8	MPa	22°C · Extrusion/Tubing · F · ASTM B 107 · L · t=0.028-0.750 wall in
Yield Strength (0.2% offset)(σy)3 entries	213.7	MPa	22°C · Bar/Extrusion/Rod · F · ASTM B 107 · L · t=All in
↳	193.1	MPa	22°C · Extruded hollow shapes · F · ASTM B 107 · L · t=All in
↳	193.1	MPa	22°C · Extrusion/Tubing · F · ASTM B 107 · L · t=0.028-0.750 wall in
Young's Modulus(E)	44.82	GPa	22°C · Bar/Extrusion/Rod

N entriesMultiple entries per property — large groups are collapsed; click a summary row to expand. Use filters above to narrow by form, heat treatment, basis, or test environment.

Rows with are inherited from the base material

Verified Unverified Low confidence (<80%) Link to source

1 interactive curve for this material

Stress-strain, S-N fatigue and environmental knockdown curves are free with an account.

Create free account

Property	Value	Unit	Conditions	Source
Thermal Conductivity vs Temperature(k(T))	Curve (4 pts)	W/(m·K)	—

Rows with are inherited from the base material

Verified Unverified Low confidence (<80%) Link to source

Property	Value	Unit	Conditions	Source
Density(ρ)	1.824	kg/m³	22°C

Rows with are inherited from the base material

Verified Unverified Low confidence (<80%) Link to source

Regulatory Screening

Environmental

Export Control

RoHS, REACH, and Prop 65 statuses are validated against official substance lists (ECHA SVHC Candidate List, OEHHA Prop 65, RoHS Annex II). Other regulations are estimated from composition and material classification. All screening is a starting point for due diligence — always verify with your supplier before making compliance decisions.

ZK60A F

Mechanical Properties

Thermal Properties

Physical Properties

Regulatory Screening

Environmental

Export Control