Polypropylene printed by fused deposition modeling is a semi-crystalline polyolefin thermoplastic extruded from filament and built up layer by layer. Its high crystallization shrinkage makes warping and corner lift common, so printing usually needs a heated bed, a surface it adheres to, and often an enclosed chamber. Parts are anisotropic, with weaker bonding between layers than along the deposited paths, visible layer lines, and marks where supports touch. Voids between beads depend on infill and settings. Printed parts serve as chemically resistant housings, fluid-handling fixtures, living hinges, lightweight jigs, and prototypes of molded parts.
Compliance & Regulations
Each row is one condition this material was measured in. Its values and curves are in the tables and charts below, labelled with the condition; the ranges here span that row's own cited values and are never averaged across rows.
| Condition | Yield (MPa) | UTS (MPa) | Elongation (%) | E (GPa) | Density (kg/m³) | Values | Curves |
|---|---|---|---|---|---|---|---|
| UltiMaker PP | 8–13 | 8–9 | 18.2–800.0 | 0 | 890 | 22 | 0 |
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Notched Charpy Impact Strength(acN) | 49.10 range 45.90–52.30 | kJ/m² | UltiMaker PP · 23°C · ISO 179-1 / 1eB (notched) · XY | ||
Elongation at Break(εf)3 entries | 800 | % | UltiMaker PP · ASTM D3039 (50 mm / min) · XY | ||
| ↳ | 800 | % | UltiMaker PP · ASTM D3039 (50 mm / min) | ||
| ↳ | 22.80 range 18.20–27.40 | % | UltiMaker PP · ASTM D3039 (50 mm / min) · Z | ||
Flexural Modulus(Ef)3 entries | 293.0 range 280.0–306.0 | MPa | UltiMaker PP · ISO 178 (1 mm / min) · XY | ||
| ↳ | 250.0 range 241.0–259.0 | MPa | UltiMaker PP · ISO 178 (1 mm / min) | ||
| ↳ | 212.0 range 203.0–221.0 | MPa | UltiMaker PP · ISO 178 (1 mm / min) · Z | ||
Flexural Strength (MOR)(σf)3 entries | 15.30 range 14.80–15.80 | MPa | UltiMaker PP · ISO 178 (5 mm / min) · XY | ||
| ↳ | 12.90 range 12.40–13.40 | MPa | UltiMaker PP · ISO 178 (5 mm / min) | ||
| ↳ | 9.400 range 9.100–9.700 | MPa | UltiMaker PP · ISO 178 (5 mm / min) · Z | ||
Hardness (Shore D)(Shore D) | 42.00 | Shore D | UltiMaker PP · ISO 7619-1 · XY | ||
Ultimate Tensile Strength(σUTS) | 8.200 range 7.900–8.500 | MPa | UltiMaker PP · ASTM D3039 (50 mm / min) · Z | ||
Yield Strength (0.2% offset)(σy)3 entries | 10.20 range 9.600–10.80 | MPa | UltiMaker PP · ASTM D3039 (50 mm / min) · XY | ||
| ↳ | 12.10 range 11.20–13.00 | MPa | UltiMaker PP · ASTM D3039 (50 mm / min) | ||
| ↳ | 8.600 range 8.200–9.000 | MPa | UltiMaker PP · ASTM D3039 (50 mm / min) · Z | ||
Young's Modulus(E)3 entries | 253.0 range 237.0–269.0 | MPa | UltiMaker PP · ASTM D3039 (1 mm / min) · XY | ||
| ↳ | 273.0 range 266.0–280.0 | MPa | UltiMaker PP · ASTM D3039 (1 mm / min) | ||
| ↳ | 234.0 range 218.0–250.0 | MPa | UltiMaker PP · ASTM D3039 (1 mm / min) · Z |
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Glass Transition Temperature(Tg) | 273.3 | K | — | ||
Heat Deflection Temperature(HDT) | 337.3 range 333.7–340.9 | K | UltiMaker PP · 0.45 MPa load · ISO 75-2 / B | ||
Melting Point / Solidus(Tm)2 entries | 403.8 | K | UltiMaker PP · ISO 11357 (DSC, 10 °C / min) | ||
| ↳ | 434.7 | K | — | ||
Vicat Softening Temperature(VST) | 372.2 range 371.5–372.9 | K | UltiMaker PP · ISO 306 / A120 |
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Density(ρ) | 890 | kg/m³ | UltiMaker PP · ISO 1183 |
Reference data from cited sources. Not verified or certified by MatWorld Inc. Verify against the source before use in design. Terms: engineering data