PEI (FDM, Roboze ULTEM AM9085F, conditioned) — Properties & Data | MatWorld

PEI (FDM, Roboze ULTEM AM9085F, conditioned)

· ULTEM AM9085F

Roboze ULTEM AM9085F is a polyetherimide blend filament grade printed by fused deposition modeling in a heated build chamber and taken in the conditioned state, brought to moisture and temperature equilibrium after printing. Printed parts are anisotropic, weaker across layers than along the deposited roads, with visible layer lines and some porosity between roads. The filament must be dried before printing, and overhangs need support material that is removed afterwards. Parts serve as aircraft interior components, ducting, brackets, and jigs, fixtures and tooling for elevated-temperature service. Every value on this page is read from Roboze's own material data sheet — quoted, cited and dated — and is the maker's statement about printed material, not a measurement by MatWorld; none has yet been reviewed by a person.

aircraft interior componentsductingbracketsjigsfixturestooling

Compliance & Regulations

?UL 94?ITAR?EAR?ISO 10993?Conflict Free?FDA?RoHS?REACH

PEI (FDM)/PEI (FDM, Roboze ULTEM AM9085F, conditioned)

Units:

si imperial

Property OverviewNormalized to typical max values

Filter by

Orientation

Specification

Property	Value	Unit	Conditions
Compressive Strength(σc)2 entries	93.00	MPa	25°C · conditioned · ASTM D695 · XZ
↳	98.00	MPa	25°C · conditioned · ASTM D695 · Z
Elongation at Break(εf)3 entries	6.800 range 6.730–6.870	%	25°C · conditioned · ASTM D638 · XZ
↳	6.600 range 6.540–6.660	%	25°C · conditioned · ASTM D638 · XY
↳	4.200 range 4.110–4.290	%	25°C · conditioned · ASTM D638 · Z
Flexural Modulus(Ef)3 entries	2.300	GPa	25°C · conditioned · ASTM D790 · XZ
↳	2.300	GPa	25°C · conditioned · ASTM D790 · XY
↳	1.400	GPa	25°C · conditioned · ASTM D790 · Z
Flexural Strength (MOR)(σf)3 entries	62.50	MPa	25°C · conditioned · ASTM D790 · XZ
↳	57.00	MPa	25°C · conditioned · ASTM D790 · XY
↳	48.00	MPa	25°C · conditioned · ASTM D790 · Z
Ultimate Tensile Strength(σUTS)3 entries	89.00 range 88.60–89.40	MPa	25°C · conditioned · ASTM D638 · XZ
↳	86.00 range 85.10–86.90	MPa	25°C · conditioned · ASTM D638 · XY
↳	66.00 range 65.60–66.40	MPa	25°C · conditioned · ASTM D638 · Z
Young's Modulus(E)3 entries	2.500 range 2.470–2.530	GPa	25°C · conditioned · ASTM D638 · XZ
↳	2.500 range 2.400–2.600	GPa	25°C · conditioned · ASTM D638 · XY
↳	2.400 range 2.320–2.480	GPa	25°C · conditioned · ASTM D638 · Z

N entriesMultiple entries per property — large groups are collapsed; click a summary row to expand. Use filters above to narrow by form, heat treatment, basis, or test environment.

Verified Unverified Low confidence (<80%) Link to source

Property	Value	Unit	Conditions	Source
Glass Transition Temperature(Tg)	486.8	K	—
Melting Point / Solidus(Tm)	391.1	K	—

Rows with are inherited from the base material

Verified Unverified Low confidence (<80%) Link to source

Reference data from cited sources. Not verified or certified by MatWorld Inc. Verify against the source before use in design. Terms: engineering data

Regulatory Screening

Environmental

Export Control

Safety & Biocompatibility

Quality & Standards

Industry-Specific

RoHS, REACH, and Prop 65 statuses are validated against official substance lists (ECHA SVHC Candidate List, OEHHA Prop 65, RoHS Annex II). Other regulations are estimated from composition and material classification. All screening is a starting point for due diligence — always verify with your supplier before making compliance decisions.