Inconel X-750 Equalized and aged
VerifiedmetalInconel X-750 is a precipitation-hardened nickel-iron-base superalloy strengthened by gamma-double-prime (γ″) phase, designed for high-temperature applications in gas turbines, jet engines, and aerospace components requiring sustained strength to approximately 1300°F (704°C). The equalized and aged condition provides optimized strength and creep resistance through controlled heat treatment, with tensile yield strength typically in the 140–160 ksi range and superior bearing and shear strength characteristics suitable for critical fasteners and structural components.
aerospacestructural
Compliance & Regulations
?ITAR?EAR?Conflict Free?RoHS?REACH?TSCA?Prop 65
Property OverviewNormalized to typical max values
Filter by
Form
Thickness
e/D Ratio
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Ultimate Bearing Strength(Fbru)4 entries | 1.703 | GPa | 22°C · Bar/Forging · Equalized and aged · AMS 5667 · t=<4.000 in · e/D=1.5 | ||
| ↳ | 1.655 | GPa | 22°C · Bar/Forging · Equalized and aged · AMS 5667 · t=4.000-10.000 in · e/D=1.5 | ||
| ↳ | 2.158 | GPa | 22°C · Bar/Forging · Equalized and aged · AMS 5667 · t=<4.000 in · e/D=2 | ||
| ↳ | 2.096 | GPa | 22°C · Bar/Forging · Equalized and aged · AMS 5667 · t=4.000-10.000 in · e/D=2 | ||
Bearing Yield Strength(Fbry)4 entries | 1.082 | GPa | 22°C · Bar/Forging · Equalized and aged · AMS 5667 · t=<4.000 in · e/D=1.5 | ||
| ↳ | 1.034 | GPa | 22°C · Bar/Forging · Equalized and aged · AMS 5667 · t=4.000-10.000 in · e/D=1.5 | ||
| ↳ | 1.303 | GPa | 22°C · Bar/Forging · Equalized and aged · AMS 5667 · t=<4.000 in · e/D=2 | ||
| ↳ | 1.241 | GPa | 22°C · Bar/Forging · Equalized and aged · AMS 5667 · t=4.000-10.000 in · e/D=2 | ||
Compressive Modulus(Ec) | 211.0 | GPa | 22°C · Strip | ||
Compressive Yield Strength(Fcy)2 entries | 723.9 | MPa | 22°C · Bar/Forging · Equalized and aged · AMS 5667 · L · t=<4.000 in | ||
| ↳ | 689.5 | MPa | 22°C · Bar/Forging · Equalized and aged · AMS 5667 · L · t=4.000-10.000 in | ||
Elongation at Break(εf)2 entries | 20.00 | - | 22°C · Bar/Forging · Equalized and aged · AMS 5667 · L · t=<4.000 in | ||
| ↳ | 15.00 | - | 22°C · Bar/Forging · Equalized and aged · AMS 5667 · L · t=4.000-10.000 in | ||
Poisson's Ratio(ν) | 0.3000 | - | 22°C | ||
Reduction of Area(RA)2 entries | 25.00 | - | 22°C · Bar/Forging · Equalized and aged · AMS 5667 · L · t=<4.000 in | ||
| ↳ | 17.00 | - | 22°C · Bar/Forging · Equalized and aged · AMS 5667 · L · t=4.000-10.000 in | ||
Shear Modulus(G) | 81.36 | GPa | 22°C · Strip | ||
Ultimate Shear Strength(Fsu)2 entries | 703.3 | MPa | 22°C · Bar/Forging · Equalized and aged · AMS 5667 · t=<4.000 in | ||
| ↳ | 682.6 | MPa | 22°C · Bar/Forging · Equalized and aged · AMS 5667 · t=4.000-10.000 in | ||
Ultimate Tensile Strength(σUTS)2 entries | 1.138 | GPa | 22°C · Bar/Forging · Equalized and aged · AMS 5667 · L · t=<4.000 in | ||
| ↳ | 1.103 | GPa | 22°C · Bar/Forging · Equalized and aged · AMS 5667 · L · t=4.000-10.000 in | ||
Yield Strength (0.2% offset)(σy)2 entries | 723.9 | MPa | 22°C · Bar/Forging · Equalized and aged · AMS 5667 · L · t=<4.000 in | ||
| ↳ | 689.5 | MPa | 22°C · Bar/Forging · Equalized and aged · AMS 5667 · L · t=4.000-10.000 in | ||
Young's Modulus(E) | 211.0 | GPa | 22°C · Strip |
N entriesMultiple entries per property — large groups are collapsed; click a summary row to expand. Use filters above to narrow by form / heat treatment / basis.
Rows with are inherited from the base material
Verified Unverified Low confidence (<80%) Link to source
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
CTE vs Temperature(α(T)) | Curve (14 pts) | 1/K | — | ||
Specific Heat vs Temperature(Cp(T)) | Curve (11 pts) | J/(kg·K) | — |
Rows with are inherited from the base material
Verified Unverified Low confidence (<80%) Link to source
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Density(ρ) | 8.249 | kg/m³ | 22°C |
Rows with are inherited from the base material
Verified Unverified Low confidence (<80%) Link to source
Regulatory Screening
Environmental
Export Control
Quality & Standards
Industry-Specific
RoHS, REACH, and Prop 65 statuses are validated against official substance lists (ECHA SVHC Candidate List, OEHHA Prop 65, RoHS Annex II). Other regulations are estimated from composition and material classification. All screening is a starting point for due diligence — always verify with your supplier before making compliance decisions.