Inconel 718 is a nickel-base superalloy containing chromium, iron, niobium, and molybdenum, designed for high-temperature structural applications in jet engines, gas turbines, and aerospace components requiring strength retention to approximately 650°C (1200°F). The ST (solution-treated) condition, produced via investment casting per AMS 5383, provides controlled mechanical properties including yield strength, ultimate tensile strength, and bearing strength suitable for critical fasteners and bearing applications with intermediate ductility.
Compliance & Regulations
10 interactive curves for this material
Stress-strain, S-N fatigue and environmental knockdown curves are free with an account.
Create free account| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Ultimate Bearing Strength(Fbru)2 entries | 1.393 | GPa | 22°C · Investment Casting · ST · AMS 5383 · t=≤0.500 in · e/D=1.5 | ||
| ↳ | 1.710 | GPa | 22°C · Investment Casting · ST · AMS 5383 · t=≤0.500 in · e/D=2 | ||
Bearing Yield Strength(Fbry)2 entries | 1.110 | GPa | 22°C · Investment Casting · ST · AMS 5383 · t=≤0.500 in · e/D=1.5 | ||
| ↳ | 1.296 | GPa | 22°C · Investment Casting · ST · AMS 5383 · t=≤0.500 in · e/D=2 | ||
Compressive Modulus(Ec) | 213.0 | GPa | 22°C · Sheet | ||
Compressive Tangent Modulus vs Stress(Etn(σ)) | Curve (12 pts) | Pa | 21°C · L | ||
Compressive Yield Strength(Fcy) | 723.9 | MPa | 22°C · Investment Casting · ST · AMS 5383 · t=≤0.500 in | ||
Elongation at Break(εf) | 3.000 | - | 22°C · Investment Casting · ST · AMS 5383 · t=≤0.500 in | ||
Fatigue Crack Growth Rate(da/dN) | Curve (6 pts) | m/cycle | 538°C | ||
Fracture Toughness(KIC) | 104,000,000 | Pa·√m | — | — | |
Hardness (Vickers)(HV) | 390 | HV | — | — | |
Poisson's Ratio(ν) | 0.2840 | - | — | — | |
Poisson's Ratio vs Temperature(ν(T)) | Curve (17 pts) | - | — | ||
Reduction of Area(RA) | 8.000 | - | 22°C · Investment Casting · ST · AMS 5383 · t=≤0.500 in | ||
Shear Modulus(G) | 78.60 | GPa | 22°C · Sheet | ||
Ultimate Shear Strength(Fsu) | 606.7 | MPa | 22°C · Investment Casting · ST · AMS 5383 · t=≤0.500 in | ||
S–N Curve (Wöhler)(S–N) | Curve (40 pts) | Pa | 538°C · LT | ||
Stress Rupture Curve(σr(t)) | Curve (12 pts) | Pa | 538°C | ||
Stress–Strain Curve(σ–ε) | Curve (11 pts) | Pa | 20°C | ||
Stress–Strain Curve (buckling region, ≤ 2% strain)(σ–ε (low-strain)) | Curve (10 pts) | Pa | 21°C · L | ||
Ultimate Tensile Strength(σUTS) | 827.4 | MPa | 22°C · Investment Casting · ST · AMS 5383 · t=≤0.500 in | ||
UTS vs Time (Creep Strength)(Ftu(t)) | Curve (16 pts) | Pa | 538°C | ||
Yield Strength (0.2% offset)(σy) | 723.9 | MPa | 22°C · Investment Casting · ST · AMS 5383 · t=≤0.500 in | ||
Yield Strength vs Temperature(σy(T)) | Curve (8 pts) | Pa | — | ||
Young's Modulus(E) | 172.0 | GPa | 649°C | — | |
Young's Modulus vs Temperature(E(T)) | Curve (8 pts) | Pa | — |
2 interactive curves for this material
Stress-strain, S-N fatigue and environmental knockdown curves are free with an account.
Create free account| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
CTE vs Temperature(α(T)) | Curve (10 pts) | 1/K | — | ||
Specific Heat Capacity(Cp) | 435 | J/(kg·K) | — | — | |
Thermal Conductivity(k) | 11.40 | W/(m·K) | 22°C | — | |
Thermal Conductivity vs Temperature(k(T)) | Curve (8 pts) | W/(m·K) | — |
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Density(ρ) | 8.190 | kg/m³ | — | — |