Inconel 600 is a nickel-chromium austenitic superalloy with excellent oxidation and corrosion resistance up to 1100°C, used in aerospace, chemical processing, and nuclear applications. The annealed condition provides optimal ductility and corrosion resistance with reduced yield strength compared to cold-worked tempers, making it suitable for applications requiring high toughness and resistance to intergranular corrosion in service temperatures up to approximately 900°C.
Compliance & Regulations
7 interactive curves for this material
Stress-strain, S-N fatigue and environmental knockdown curves are free with an account.
Create free account| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Ultimate Bearing Strength(Fbru)4 entries | 1.048 | GPa | 22°C · Bar/Rod · Annealed · ASTM B166 · t=All in · e/D=2 | ||
| ↳ | 1.048 | GPa | 22°C · Sheet/Strip/Plate · Annealed · AMS 5540 · t=0.020-2.000 in · e/D=2 | ||
| ↳ | 1.048 | GPa | 22°C · Forging · Annealed · ASTM B564 · e/D=2 | ||
| ↳ | Curve (10 pts) | Pa | — | ||
Compressive Modulus(Ec) | Curve (8 pts) | Pa | L | ||
Compressive Yield Strength(Fcy)4 entries | 241.3 | MPa | 22°C · Bar/Rod · Annealed · ASTM B166 · L · t=All in | ||
| ↳ | 241.3 | MPa | 22°C · Forging · Annealed · ASTM B564 · L | ||
| ↳ | 241.3 | MPa | 22°C · Sheet/Strip/Plate · Annealed · AMS 5540 · LT · t=0.020-2.000 in | ||
| ↳ | Curve (9 pts) | Pa | L | ||
Elongation at Break(εf)3 entries | 30.00 | - | 22°C · Bar/Rod · Annealed · ASTM B166 · L · t=All in | ||
| ↳ | 30.00 | - | 22°C · Forging · Annealed · ASTM B564 · L | ||
| ↳ | 30.00 | - | 22°C · Sheet/Strip/Plate · Annealed · AMS 5540 · LT · t=0.020-2.000 in | ||
Poisson's Ratio(ν) | 0.2900 | - | 22°C | ||
Shear Modulus(G) | 75.84 | GPa | 22°C · Round | ||
Ultimate Shear Strength(Fsu)4 entries | 351.6 | MPa | 22°C · Bar/Rod · Annealed · ASTM B166 · t=All in | ||
| ↳ | 351.6 | MPa | 22°C · Sheet/Strip/Plate · Annealed · AMS 5540 · t=0.020-2.000 in | ||
| ↳ | 351.6 | MPa | 22°C · Forging · Annealed · ASTM B564 | ||
| ↳ | Curve (11 pts) | Pa | — | ||
Ultimate Tensile Strength(σUTS)4 entries | 551.6 | MPa | 22°C · Bar/Rod · Annealed · ASTM B166 · L · t=All in | ||
| ↳ | 551.6 | MPa | 22°C · Forging · Annealed · ASTM B564 · L | ||
| ↳ | 551.6 | MPa | 22°C · Sheet/Strip/Plate · Annealed · AMS 5540 · LT · t=0.020-2.000 in | ||
| ↳ | Curve (14 pts) | Pa | L | ||
Yield Strength (0.2% offset)(σy)4 entries | 241.3 | MPa | 22°C · Bar/Rod · Annealed · ASTM B166 · L · t=All in | ||
| ↳ | 241.3 | MPa | 22°C · Forging · Annealed · ASTM B564 · L | ||
| ↳ | 241.3 | MPa | 22°C · Sheet/Strip/Plate · Annealed · AMS 5540 · LT · t=0.020-2.000 in | ||
| ↳ | Curve (12 pts) | Pa | L | ||
Young's Modulus(E) | Curve (8 pts) | Pa | L |
3 interactive curves for this material
Stress-strain, S-N fatigue and environmental knockdown curves are free with an account.
Create free account| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
CTE vs Temperature(α(T)) | Curve (7 pts) | 1/K | — | ||
Specific Heat vs Temperature(Cp(T)) | Curve (8 pts) | J/(kg·K) | — | ||
Thermal Conductivity vs Temperature(k(T)) | Curve (8 pts) | W/(m·K) | — |
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Density(ρ) | 8.415 | kg/m³ | 22°C |