Inconel 600 Annealed
VerifiedmetalUNS N06600
Inconel 600 is a nickel-chromium austenitic superalloy with excellent oxidation and corrosion resistance up to 1100°C, used in aerospace, chemical processing, and nuclear applications. The annealed condition provides optimal ductility and corrosion resistance with reduced yield strength compared to cold-worked tempers, making it suitable for applications requiring high toughness and resistance to intergranular corrosion in service temperatures up to approximately 900°C.
aerospacestructural
Compliance & Regulations
?ITAR?EAR?Conflict Free?RoHS?REACH?TSCA?Prop 65
Property OverviewNormalized to typical max values
Filter by
Form
Thickness
Orientation
Specification
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Ultimate Bearing Strength(Fbru)4 entries | 1.048 | GPa | 22°C · Bar/Rod · Annealed · ASTM B166 · t=All in · e/D=2 | ||
| ↳ | 1.048 | GPa | 22°C · Sheet/Strip/Plate · Annealed · AMS 5540 · t=0.020-2.000 in · e/D=2 | ||
| ↳ | 1.048 | GPa | 22°C · Forging · Annealed · ASTM B564 · e/D=2 | ||
| ↳ | Curve (10 pts) | Pa | — | ||
Compressive Modulus(Ec) | Curve (8 pts) | Pa | L | ||
Compressive Yield Strength(Fcy)4 entries | 241.3 | MPa | 22°C · Bar/Rod · Annealed · ASTM B166 · L · t=All in | ||
| ↳ | 241.3 | MPa | 22°C · Forging · Annealed · ASTM B564 · L | ||
| ↳ | 241.3 | MPa | 22°C · Sheet/Strip/Plate · Annealed · AMS 5540 · LT · t=0.020-2.000 in | ||
| ↳ | Curve (9 pts) | Pa | L | ||
Elongation at Break(εf)3 entries | 30.00 | - | 22°C · Bar/Rod · Annealed · ASTM B166 · L · t=All in | ||
| ↳ | 30.00 | - | 22°C · Forging · Annealed · ASTM B564 · L | ||
| ↳ | 30.00 | - | 22°C · Sheet/Strip/Plate · Annealed · AMS 5540 · LT · t=0.020-2.000 in | ||
Poisson's Ratio(ν) | 0.2900 | - | 22°C | ||
Shear Modulus(G) | 75.84 | GPa | 22°C · Round | ||
Ultimate Shear Strength(Fsu)4 entries | 351.6 | MPa | 22°C · Bar/Rod · Annealed · ASTM B166 · t=All in | ||
| ↳ | 351.6 | MPa | 22°C · Sheet/Strip/Plate · Annealed · AMS 5540 · t=0.020-2.000 in | ||
| ↳ | 351.6 | MPa | 22°C · Forging · Annealed · ASTM B564 | ||
| ↳ | Curve (11 pts) | Pa | — | ||
Ultimate Tensile Strength(σUTS)4 entries | 551.6 | MPa | 22°C · Bar/Rod · Annealed · ASTM B166 · L · t=All in | ||
| ↳ | 551.6 | MPa | 22°C · Forging · Annealed · ASTM B564 · L | ||
| ↳ | 551.6 | MPa | 22°C · Sheet/Strip/Plate · Annealed · AMS 5540 · LT · t=0.020-2.000 in | ||
| ↳ | Curve (14 pts) | Pa | L | ||
Yield Strength (0.2% offset)(σy)4 entries | 241.3 | MPa | 22°C · Bar/Rod · Annealed · ASTM B166 · L · t=All in | ||
| ↳ | 241.3 | MPa | 22°C · Forging · Annealed · ASTM B564 · L | ||
| ↳ | 241.3 | MPa | 22°C · Sheet/Strip/Plate · Annealed · AMS 5540 · LT · t=0.020-2.000 in | ||
| ↳ | Curve (12 pts) | Pa | L | ||
Young's Modulus(E) | Curve (8 pts) | Pa | L |
N entriesMultiple entries per property — large groups are collapsed; click a summary row to expand. Use filters above to narrow by form / heat treatment / basis.
Rows with are inherited from the base material
Verified Unverified Low confidence (<80%) Link to source
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
CTE vs Temperature(α(T)) | Curve (7 pts) | 1/K | — | ||
Specific Heat vs Temperature(Cp(T)) | Curve (8 pts) | J/(kg·K) | — | ||
Thermal Conductivity vs Temperature(k(T)) | Curve (8 pts) | W/(m·K) | — |
Verified Unverified Low confidence (<80%) Link to source
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Density(ρ) | 8.415 | kg/m³ | 22°C |
Rows with are inherited from the base material
Verified Unverified Low confidence (<80%) Link to source
Regulatory Screening
Environmental
Export Control
Quality & Standards
Industry-Specific
RoHS, REACH, and Prop 65 statuses are validated against official substance lists (ECHA SVHC Candidate List, OEHHA Prop 65, RoHS Annex II). Other regulations are estimated from composition and material classification. All screening is a starting point for due diligence — always verify with your supplier before making compliance decisions.