Custom 465 stainless steel is a precipitation-hardened martensitic stainless steel containing cobalt and molybdenum, designed for high-strength aerospace applications requiring exceptional fatigue resistance and bearing performance. The H1000 condition provides maximum hardness and strength through precipitation hardening, delivering ultimate tensile strengths in the 1900+ MPa range with good corrosion resistance and dimensional stability at elevated temperatures.
Compliance & Regulations
4 interactive curves for this material
Stress-strain, S-N fatigue and environmental knockdown curves are free with an account.
Create free account| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Ultimate Bearing Strength(Fbru)4 entries | 333 | ksi | 22°C · Bar · H1000 · AMS 5936 · t=≤12.000 in · e/D=1.5 | ||
| ↳ | 342 | ksi | 22°C · Bar · H1000 · AMS 5936 · t=≤12.000 in · e/D=1.5 | ||
| ↳ | 428 | ksi | 22°C · Bar · H1000 · AMS 5936 · t=≤12.000 in · e/D=2 | ||
| ↳ | 440 | ksi | 22°C · Bar · H1000 · AMS 5936 · t=≤12.000 in · e/D=2 | ||
Bearing Yield Strength(Fbry)4 entries | 294 | ksi | 22°C · Bar · H1000 · AMS 5936 · t=≤12.000 in · e/D=1.5 | ||
| ↳ | 312 | ksi | 22°C · Bar · H1000 · AMS 5936 · t=≤12.000 in · e/D=1.5 | ||
| ↳ | 353 | ksi | 22°C · Bar · H1000 · AMS 5936 · t=≤12.000 in · e/D=2 | ||
| ↳ | 374 | ksi | 22°C · Bar · H1000 · AMS 5936 · t=≤12.000 in · e/D=2 | ||
Compressive Modulus(Ec) | 28,900 | ksi | 22°C · Bar | ||
Compressive Yield Strength(Fcy)4 entries | 210 | ksi | 22°C · Bar · H1000 · AMS 5936 · L · t=≤12.000 in | ||
| ↳ | 223 | ksi | 22°C · Bar · H1000 · AMS 5936 · L · t=≤12.000 in | ||
| ↳ | 211 | ksi | 22°C · Bar · H1000 · AMS 5936 · LT · t=≤12.000 in | ||
| ↳ | 224 | ksi | 22°C · Bar · H1000 · AMS 5936 · LT · t=≤12.000 in | ||
Elongation at Break(εf)2 entries | 10.00 | - | 22°C · Bar · H1000 · AMS 5936 · L · t=≤12.000 in | ||
| ↳ | 10.00 | - | 22°C · Bar · H1000 · AMS 5936 · LT · t=≤12.000 in | ||
Poisson's Ratio(ν) | 0.2800 | - | 22°C | ||
Reduction of Area(RA)2 entries | 50.00 | - | 22°C · Bar · H1000 · AMS 5936 · L · t=≤12.000 in | ||
| ↳ | 40.00 | - | 22°C · Bar · H1000 · AMS 5936 · LT · t=≤12.000 in | ||
Shear Modulus(G) | 11,200 | ksi | 22°C · Bar | ||
Ultimate Shear Strength(Fsu)2 entries | 129 | ksi | 22°C · Bar · H1000 · AMS 5936 · t=≤12.000 in | ||
| ↳ | 132 | ksi | 22°C · Bar · H1000 · AMS 5936 · t=≤12.000 in | ||
Stress–Strain Curve(σ–ε)2 entries | Curve (29 pts) | ksi | 21°C · L | ||
| ↳ | Curve (29 pts) | ksi | 21°C · LT | ||
Stress–Strain Curve (buckling region, ≤ 2% strain)(σ–ε (low-strain))2 entries | Curve (33 pts) | ksi | 21°C · L | ||
| ↳ | Curve (33 pts) | ksi | 21°C · LT | ||
Ultimate Tensile Strength(σUTS)4 entries | 220 | ksi | 22°C · Bar · H1000 · AMS 5936 · L · t=≤12.000 in | ||
| ↳ | 226 | ksi | 22°C · Bar · H1000 · AMS 5936 · L · t=≤12.000 in | ||
| ↳ | 220 | ksi | 22°C · Bar · H1000 · AMS 5936 · LT · t=≤12.000 in | ||
| ↳ | 226 | ksi | 22°C · Bar · H1000 · AMS 5936 · LT · t=≤12.000 in | ||
Yield Strength (0.2% offset)(σy)4 entries | 200 | ksi | 22°C · Bar · H1000 · AMS 5936 · L · t=≤12.000 in | ||
| ↳ | 212 | ksi | 22°C · Bar · H1000 · AMS 5936 · L · t=≤12.000 in | ||
| ↳ | 200 | ksi | 22°C · Bar · H1000 · AMS 5936 · LT · t=≤12.000 in | ||
| ↳ | 213 | ksi | 22°C · Bar · H1000 · AMS 5936 · LT · t=≤12.000 in | ||
Young's Modulus(E) | 28,700 | ksi | 22°C · Bar |
3 interactive curves for this material
Stress-strain, S-N fatigue and environmental knockdown curves are free with an account.
Create free account| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
CTE vs Temperature(α(T)) | Curve (6 pts) | µin/in·°F | — | ||
Specific Heat vs Temperature(Cp(T)) | Curve (7 pts) | BTU/(lb·°F) | — | ||
Thermal Conductivity vs Temperature(k(T)) | Curve (7 pts) | BTU/(hr·ft·°F) | — |
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Density(ρ) | 0.2800 | lb/in³ | 22°C |