Custom 465 Stainless Steel H1000
VerifiedmetalCustom 465 stainless steel is a precipitation-hardened martensitic stainless steel containing cobalt and molybdenum, designed for high-strength aerospace applications requiring exceptional fatigue resistance and bearing performance. The H1000 condition provides maximum hardness and strength through precipitation hardening, delivering ultimate tensile strengths in the 1900+ MPa range with good corrosion resistance and dimensional stability at elevated temperatures.
aerospacestructural
Compliance & Regulations
?Conflict Free?RoHS?REACH?TSCA?Prop 65
Property OverviewNormalized to typical max values
Filter by
e/D Ratio
Basis
Orientation
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Ultimate Bearing Strength(Fbru)4 entries | 2.296 | GPa | 22°C · Bar · H1000 · AMS 5936 · t=≤12.000 in · e/D=1.5 | ||
| ↳ | 2.358 | GPa | 22°C · Bar · H1000 · AMS 5936 · t=≤12.000 in · e/D=1.5 | ||
| ↳ | 2.951 | GPa | 22°C · Bar · H1000 · AMS 5936 · t=≤12.000 in · e/D=2 | ||
| ↳ | 3.034 | GPa | 22°C · Bar · H1000 · AMS 5936 · t=≤12.000 in · e/D=2 | ||
Bearing Yield Strength(Fbry)4 entries | 2.027 | GPa | 22°C · Bar · H1000 · AMS 5936 · t=≤12.000 in · e/D=1.5 | ||
| ↳ | 2.151 | GPa | 22°C · Bar · H1000 · AMS 5936 · t=≤12.000 in · e/D=1.5 | ||
| ↳ | 2.434 | GPa | 22°C · Bar · H1000 · AMS 5936 · t=≤12.000 in · e/D=2 | ||
| ↳ | 2.579 | GPa | 22°C · Bar · H1000 · AMS 5936 · t=≤12.000 in · e/D=2 | ||
Compressive Modulus(Ec) | 199.3 | GPa | 22°C · Bar | ||
Compressive Yield Strength(Fcy)4 entries | 1.448 | GPa | 22°C · Bar · H1000 · AMS 5936 · L · t=≤12.000 in | ||
| ↳ | 1.538 | GPa | 22°C · Bar · H1000 · AMS 5936 · L · t=≤12.000 in | ||
| ↳ | 1.455 | GPa | 22°C · Bar · H1000 · AMS 5936 · LT · t=≤12.000 in | ||
| ↳ | 1.544 | GPa | 22°C · Bar · H1000 · AMS 5936 · LT · t=≤12.000 in | ||
Elongation at Break(εf)2 entries | 10.00 | - | 22°C · Bar · H1000 · AMS 5936 · L · t=≤12.000 in | ||
| ↳ | 10.00 | - | 22°C · Bar · H1000 · AMS 5936 · LT · t=≤12.000 in | ||
Poisson's Ratio(ν) | 0.2800 | - | 22°C | ||
Reduction of Area(RA)2 entries | 50.00 | - | 22°C · Bar · H1000 · AMS 5936 · L · t=≤12.000 in | ||
| ↳ | 40.00 | - | 22°C · Bar · H1000 · AMS 5936 · LT · t=≤12.000 in | ||
Shear Modulus(G) | 77.22 | GPa | 22°C · Bar | ||
Ultimate Shear Strength(Fsu)2 entries | 889.4 | MPa | 22°C · Bar · H1000 · AMS 5936 · t=≤12.000 in | ||
| ↳ | 910.1 | MPa | 22°C · Bar · H1000 · AMS 5936 · t=≤12.000 in | ||
Stress–Strain Curve(σ–ε)2 entries | Curve (29 pts) | Pa | 21°C · L | ||
| ↳ | Curve (29 pts) | Pa | 21°C · LT | ||
Stress–Strain Curve (buckling region, ≤ 2% strain)(σ–ε (low-strain))2 entries | Curve (33 pts) | Pa | 21°C · L | ||
| ↳ | Curve (33 pts) | Pa | 21°C · LT | ||
Ultimate Tensile Strength(σUTS)4 entries | 1.517 | GPa | 22°C · Bar · H1000 · AMS 5936 · L · t=≤12.000 in | ||
| ↳ | 1.558 | GPa | 22°C · Bar · H1000 · AMS 5936 · L · t=≤12.000 in | ||
| ↳ | 1.517 | GPa | 22°C · Bar · H1000 · AMS 5936 · LT · t=≤12.000 in | ||
| ↳ | 1.558 | GPa | 22°C · Bar · H1000 · AMS 5936 · LT · t=≤12.000 in | ||
Yield Strength (0.2% offset)(σy)4 entries | 1.379 | GPa | 22°C · Bar · H1000 · AMS 5936 · L · t=≤12.000 in | ||
| ↳ | 1.462 | GPa | 22°C · Bar · H1000 · AMS 5936 · L · t=≤12.000 in | ||
| ↳ | 1.379 | GPa | 22°C · Bar · H1000 · AMS 5936 · LT · t=≤12.000 in | ||
| ↳ | 1.469 | GPa | 22°C · Bar · H1000 · AMS 5936 · LT · t=≤12.000 in | ||
Young's Modulus(E) | 197.9 | GPa | 22°C · Bar |
N entriesMultiple entries per property — large groups are collapsed; click a summary row to expand. Use filters above to narrow by form / heat treatment / basis.
Rows with are inherited from the base material
Verified Unverified Low confidence (<80%) Link to source
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
CTE vs Temperature(α(T)) | Curve (6 pts) | 1/K | — | ||
Specific Heat vs Temperature(Cp(T)) | Curve (7 pts) | J/(kg·K) | — | ||
Thermal Conductivity vs Temperature(k(T)) | Curve (7 pts) | W/(m·K) | — |
Verified Unverified Low confidence (<80%) Link to source
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Density(ρ) | 7.750 | kg/m³ | 22°C |
Rows with are inherited from the base material
Verified Unverified Low confidence (<80%) Link to source
Regulatory Screening
Environmental
Quality & Standards
Industry-Specific
RoHS, REACH, and Prop 65 statuses are validated against official substance lists (ECHA SVHC Candidate List, OEHHA Prop 65, RoHS Annex II). Other regulations are estimated from composition and material classification. All screening is a starting point for due diligence — always verify with your supplier before making compliance decisions.