Custom 450 stainless steel is a martensitic stainless steel with approximately 13% chromium and 1% molybdenum, designed for high-strength aerospace and turbine engine applications requiring elevated temperature strength and corrosion resistance. The H1100 condition (hardened and tempered to approximately 1100°F) provides tensile strengths typically in the 180–200 ksi range with moderate elongation, balancing hardness and fracture toughness for critical rotating components.
Compliance & Regulations
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Compressive Modulus(Ec) | 213.7 | GPa | 22°C · Bar | ||
Elongation at Break(εf)2 entries | 16.00 | - | 22°C · Bar · H1100 · AMS 5773 · L · t=≤12.000 in | ||
| ↳ | 11.00 | - | 22°C · Bar · H1100 · AMS 5773 · LT · t=≤12.000 in | ||
Poisson's Ratio(ν) | 0.2900 | - | 22°C | ||
Shear Modulus(G) | 77.22 | GPa | 22°C · Bar | ||
Ultimate Tensile Strength(σUTS)2 entries | 896.3 | MPa | 22°C · Bar · H1100 · AMS 5773 · L · t=≤12.000 in | ||
| ↳ | 896.3 | MPa | 22°C · Bar · H1100 · AMS 5773 · LT · t=≤12.000 in | ||
Yield Strength (0.2% offset)(σy)2 entries | 723.9 | MPa | 22°C · Bar · H1100 · AMS 5773 · L · t=≤12.000 in | ||
| ↳ | 723.9 | MPa | 22°C · Bar · H1100 · AMS 5773 · LT · t=≤12.000 in | ||
Young's Modulus(E) | 193.1 | GPa | 22°C · Bar |
1 interactive curve for this material
Stress-strain, S-N fatigue and environmental knockdown curves are free with an account.
Create free account| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
CTE vs Temperature(α(T)) | Curve (16 pts) | 1/K | — |
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Density(ρ) | 7.750 | kg/m³ | 22°C |