Custom 450 stainless steel is a precipitation-hardened martensitic stainless steel (17% Cr, 4% Ni, 1% Mo) designed for high-strength aerospace applications requiring corrosion resistance and elevated temperature capability to approximately 600°F. The H1050 condition (solution heat-treated and aged) delivers tensile strength around 180 ksi with moderate ductility, suitable for bearing races, fasteners, and structural components in gas turbine engines and airframes per AMS 5763/5773 specifications.
Compliance & Regulations
10 interactive curves for this material
Stress-strain, S-N fatigue and environmental knockdown curves are free with an account.
Create free account| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Ultimate Bearing Strength(Fbru)4 entries | 239 | ksi | 22°C · Bar · H1050 · AMS 5763 · t=≤8.000 in · e/D=1.5 | ||
| ↳ | 307 | ksi | 22°C · Bar · H1050 · AMS 5763 · t=≤8.000 in · e/D=2 | ||
| ↳ | 239 | ksi | 22°C · Bar · H1050 · AMS 5773 · t=≤12.000 in · e/D=1.5 | ||
| ↳ | 307 | ksi | 22°C · Bar · H1050 · AMS 5773 · t=≤12.000 in · e/D=2 | ||
Bearing Yield Strength(Fbry)4 entries | 204 | ksi | 22°C · Bar · H1050 · AMS 5763 · t=≤8.000 in · e/D=1.5 | ||
| ↳ | 257 | ksi | 22°C · Bar · H1050 · AMS 5763 · t=≤8.000 in · e/D=2 | ||
| ↳ | 204 | ksi | 22°C · Bar · H1050 · AMS 5773 · t=≤12.000 in · e/D=1.5 | ||
| ↳ | 257 | ksi | 22°C · Bar · H1050 · AMS 5773 · t=≤12.000 in · e/D=2 | ||
Compressive Modulus(Ec) | 31,000 | ksi | 22°C · Bar | ||
Compressive Yield Strength(Fcy)4 entries | 143 | ksi | 22°C · Bar · H1050 · AMS 5763 · L · t=≤8.000 in | ||
| ↳ | 141 | ksi | 22°C · Bar · H1050 · AMS 5763 · ST · t=≤8.000 in | ||
| ↳ | 143 | ksi | 22°C · Bar · H1050 · AMS 5773 · L · t=≤12.000 in | ||
| ↳ | 141 | ksi | 22°C · Bar · H1050 · AMS 5773 · LT · t=≤12.000 in | ||
Elongation at Break(εf)4 entries | 12.00 | - | 22°C · Bar · H1050 · AMS 5763 · L · t=≤8.000 in | ||
| ↳ | 12.00 | - | 22°C · Bar · H1050 · AMS 5773 · L · t=≤12.000 in | ||
| ↳ | 9.000 | - | 22°C · Bar · H1050 · AMS 5773 · LT · t=≤12.000 in | ||
| ↳ | Curve (8 pts) | - | L | ||
Poisson's Ratio(ν) | 0.2900 | - | 22°C | ||
Reduction of Area(RA) | 45.00 | - | 22°C · Bar · H1050 · AMS 5763 · L · t=≤8.000 in | ||
Reduction of Area vs Temperature(RA(T)) | Curve (11 pts) | - | L | ||
Shear Modulus(G) | 11,200 | ksi | 22°C · Bar | ||
Ultimate Shear Strength(Fsu)3 entries | 93.00 | ksi | 22°C · Bar · H1050 · AMS 5763 · t=≤8.000 in | ||
| ↳ | 93.00 | ksi | 22°C · Bar · H1050 · AMS 5773 · t=≤12.000 in | ||
| ↳ | Curve (10 pts) | ksi | — | ||
S–N Curve (Wöhler)(S–N)3 entries | Curve (40 pts) | ksi | 21°C · L | ||
| ↳ | Curve (40 pts) | ksi | 21°C · L | ||
| ↳ | Curve (40 pts) | ksi | 21°C · L | ||
Stress–Strain Curve (buckling region, ≤ 2% strain)(σ–ε (low-strain))2 entries | Curve (8 pts) | ksi | 21°C · L | ||
| ↳ | Curve (8 pts) | ksi | 21°C · LT | ||
Ultimate Tensile Strength(σUTS) | 144 – 145 | ksi | 5 entriesClick to expand | ||
Yield Strength (0.2% offset)(σy) | 133 – 135 | ksi | 5 entriesClick to expand | ||
Young's Modulus(E) | 28,000 | ksi | 22°C · Bar | ||
1 interactive curve for this material
Stress-strain, S-N fatigue and environmental knockdown curves are free with an account.
Create free account| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
CTE vs Temperature(α(T)) | Curve (16 pts) | µin/in·°F | — |
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Density(ρ) | 0.2800 | lb/in³ | 22°C |