Engineered laminate of AW280-5H/3501-6, stacked [(0/+-45/90):f]:s. Properties here are laminate-level effective values in the laminate's own axes — not the lamina constants, which live on the parent prepreg (AW280-5H/3501-6 — AS4 carbon/3501). From MIL-HDBK-17-2F Volume 2 (US Government work, public domain).
Compliance & Regulations
Fiber Direction
Ply Schedule
Laminate Code
[0/45/-45/90/90/-45/45/0]s
Fiber angles relative to the 0° reference direction (red arrow in 3D view). 0° = longitudinal, 90° = transverse, ±45° = shear paths.
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Compressive Modulus(Ec) | 59.98 range 52.40–64.81n=13, 3 batches, CV 8.2% | GPa | 24°C · RTA · 1-axis · [0:f]:8 · norm. thk+Vf | ||
Compressive Strength(σc) | 730.8 range 627.4–792.9n=13, 3 batches, CV 6.52% | MPa | 24°C · RTA · 1-axis · [0:f]:8 · norm. thk+Vf | ||
Interlaminar Shear Strength(ILSS) | 68.46 range 58.61–73.77n=9, 3 batches, CV 7.38% | MPa | 24°C · RTA · 13-axis · [0]:15 · as-measured | ||
Ultimate Tensile Strength(σUTS)2 entries | 575.0 range 521.9–608.1n=6, 2 batches, CV 5.28% | MPa | 24°C · RTA · x-axis · [(0/+-45/90):f]:s · norm. thk+Vf | ||
| ↳ | 610.9 range 560.5–649.5n=6, 2 batches, CV 4.86% | MPa | 24°C · RTA · x-axis · [(0/+-45/90):f]:s · as-measured | ||
Young's Modulus(E)2 entries | 47.57 range 45.51–48.26n=6, 2 batches, CV 2.8% | GPa | 24°C · RTA · x-axis · [(0/+-45/90):f]:s · norm. thk+Vf | ||
| ↳ | 50.33 range 48.26–51.71n=6, 2 batches, CV 2.9% | GPa | 24°C · RTA · x-axis · [(0/+-45/90):f]:s · as-measured |