AS4 (Hercules) carbon fibre in a 5250-3 (Narmco) bismaleimide matrix, supplied as tape. Carbon/BMI extends carbon/epoxy to sustained service around 350-450 °F, well beyond epoxy's limit, while processing in broadly similar tooling. It is used for engine nacelles and nozzles, structure near exhaust, and supersonic-aircraft skins subject to aerodynamic heating. The handbook characterises it from -67 °F to 450 °F, consistent with elevated-temperature service. MatWorld carries 16 tensile, compressive and shear curves for this system, digitised from MIL-HDBK-17-2F Volume 2 (US Government work, public domain).
Compliance & Regulations
Fiber Direction
Ply Schedule
Laminate Code
[0/0/0/0/0/0/0/0]s
Fiber angles relative to the 0° reference direction (red arrow in 3D view). 0° = longitudinal, 90° = transverse, ±45° = shear paths.
16 interactive curves for this material
Stress-strain, S-N fatigue and environmental knockdown curves are free with an account.
Create free account| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Compressive Modulus(Ec) | 86.87 – 156.5 | GPa | 16 entriesClick to expand | ||
Compressive Strength(σc) | 0.6750 – 1.620 | GPa | 16 entriesClick to expand | ||
Elongation at Break(εf) | 0.2000 – 2.670 | - | 20 entriesClick to expand | ||
Poisson's Ratio(ν) | 0.2950 – 0.3630 | - | 7 entriesClick to expand | ||
Shear Modulus(G) | 2.758 – 5.929 | GPa | 8 entriesClick to expand | ||
Ultimate Shear Strength(Fsu) | 56.05 – 91.01 | MPa | 8 entriesClick to expand | ||
Ultimate Tensile Strength(σUTS) | 0.02365 – 2.392 | GPa | 21 entriesClick to expand | ||
Young's Modulus(E) | 6.412 – 146.2 | GPa | 21 entriesClick to expand | ||