C355.0 is an aluminum-copper-magnesium casting alloy with silicon modification, used primarily in aerospace and high-performance applications requiring elevated temperature strength and dimensional stability. The T6 temper (solution heat-treated and artificially aged) provides tensile strengths of approximately 35–40 ksi with good bearing strength and moderate ductility, making it suitable for complex cast aerospace components operating at intermediate temperatures.
Compliance & Regulations
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Ultimate Bearing Strength(Fbru)2 entries | 482.6 | MPa | 22°C · Casting · T6 · AMS-A-21180 · e/D=1.5 | ||
| ↳ | 606.7 | MPa | 22°C · Casting · T6 · AMS-A-21180 · e/D=2 | ||
Bearing Yield Strength(Fbry)2 entries | 337.8 | MPa | 22°C · Casting · T6 · AMS-A-21180 · e/D=1.5 | ||
| ↳ | 399.9 | MPa | 22°C · Casting · T6 · AMS-A-21180 · e/D=2 | ||
Compressive Modulus(Ec) | 71.02 | GPa | 22°C · Casting | ||
Compressive Yield Strength(Fcy) | 213.7 | MPa | 22°C · Casting · T6 · AMS-A-21180 | ||
Elongation at Break(εf) | 3.000 | - | 22°C · Casting · T6 · AMS-A-21180 | ||
Poisson's Ratio(ν) | 0.3300 | - | 22°C | ||
Shear Modulus(G) | 26.54 | GPa | 22°C · Casting | ||
Ultimate Shear Strength(Fsu) | 179.3 | MPa | 22°C · Casting · T6 · AMS-A-21180 | ||
Ultimate Tensile Strength(σUTS) | 282.7 | MPa | 22°C · Casting · T6 · AMS-A-21180 | ||
Yield Strength (0.2% offset)(σy) | 213.7 | MPa | 22°C · Casting · T6 · AMS-A-21180 | ||
Young's Modulus(E) | 69.64 | GPa | 22°C · Casting |
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Density(ρ) | 2.713 | kg/m³ | 22°C |