AZ31B-H24 is a wrought magnesium alloy containing aluminum and zinc that is strain-hardened and partially annealed to provide moderate strength with improved ductility and stress-relief characteristics. The H24 temper offers tensile yield strength around 160 MPa and ultimate tensile strength around 230 MPa, making it suitable for aerospace and automotive sheet applications requiring good formability and corrosion resistance at room temperature.
Compliance & Regulations
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Compressive Modulus(Ec) | 44.82 | GPa | 22°C · Bar/Extrusion/Rod | ||
Poisson's Ratio(ν) | 0.3500 | - | 22°C | ||
Shear Modulus(G) | 16.55 | GPa | 22°C · Bar/Extrusion/Rod | ||
Young's Modulus(E) | 44.82 | GPa | 22°C · Bar/Extrusion/Rod |
3 interactive curves for this material
Stress-strain, S-N fatigue and environmental knockdown curves are free with an account.
Create free account| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
CTE vs Temperature(α(T)) | Curve (14 pts) | 1/K | — | ||
Specific Heat vs Temperature(Cp(T)) | Curve (12 pts) | J/(kg·K) | — | ||
Thermal Conductivity vs Temperature(k(T)) | Curve (13 pts) | W/(m·K) | — |
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Density(ρ) | 1.769 | kg/m³ | 22°C |