AM-355 Stainless Steel T850
VerifiedmetalAM-355 stainless steel is a martensitic stainless alloy (13% Cr, 4.7% Ni, 2.7% Mo) used in aerospace applications requiring high strength and corrosion resistance at elevated temperatures. The T850 temper (solution heat-treated and age-hardened) provides yield strengths in the 1380–1520 MPa range with good bearing strength and moderate ductility, suitable for critical fasteners, compressor components, and high-stress structural applications to approximately 315°C.
aerospacestructural
Compliance & Regulations
?Conflict Free?RoHS?REACH?TSCA?Prop 65
Filter by
Form
Heat Treatment
Thickness
Orientation
Specification
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Ultimate Bearing Strength(Fbru)2 entries | — | Pa | 22°C · Sheet/Strip · SCT850b · AMS 5547 · t=0.0005-0.187 in · e/D=2 | — | |
| ↳ | — | Pa | 22°C · Plateb · SCT850c · AMS 5549a · t=<0.375 in · e/D=2 | — | |
Bearing Yield Strength(Fbry)2 entries | — | Pa | 22°C · Sheet/Strip · SCT850b · AMS 5547 · t=0.0005-0.187 in · e/D=2 | — | |
| ↳ | — | Pa | 22°C · Plateb · SCT850c · AMS 5549a · t=<0.375 in · e/D=2 | — | |
Compressive Modulus(Ec) | — | Pa | 22°C · Sheet/Strip | — | |
Compressive Yield Strength(Fcy)3 entries | — | Pa | 22°C · Plateb · SCT850c · AMS 5549a · L · t=<0.375 in | — | |
| ↳ | — | Pa | 22°C · Sheet/Strip · SCT850b · AMS 5547 · L · t=0.0005-0.187 in | — | |
| ↳ | Curve (13 pts) | Pa | L | — | |
Elongation at Break(εf)4 entries | — | - | 22°C · Bar/Forging · SCT850b · AMS 5743 · L · t=... in | — | |
| ↳ | — | - | 22°C · Plateb · SCT850c · AMS 5549a · LT · t=<0.375 in | — | |
| ↳ | — | - | 22°C · Plateb · SCT850c · AMS 5549a · LT · t=0.375-1.000 in | — | |
| ↳ | — | - | 22°C · Plateb · SCT850c · AMS 5549a · LT · t=>1.000 in | — | |
Poisson's Ratio(ν) | — | - | 22°C | — | |
Reduction of Area(RA) | — | - | 22°C · Bar/Forging · SCT850b · AMS 5743 · L · t=... in | — | |
Shear Modulus(G) | — | Pa | 22°C · Sheet/Strip | — | |
Ultimate Shear Strength(Fsu)3 entries | — | Pa | 22°C · Plateb · SCT850c · AMS 5549a · t=<0.375 in | — | |
| ↳ | — | Pa | 22°C · Sheet/Strip · SCT850b · AMS 5547 · t=0.0005-0.187 in | — | |
| ↳ | Curve (11 pts) | Pa | — | — | |
Ultimate Tensile Strength(σUTS) | — | Pa | 8 entriesClick to expand | ||
Yield Strength (0.2% offset)(σy) | — | Pa | 7 entriesClick to expand | ||
Young's Modulus(E) | Curve (7 pts) | Pa | L | — | |
N entriesMultiple entries per property — large groups are collapsed; click a summary row to expand. Use filters above to narrow by form / heat treatment / basis.
Rows with are inherited from the base material
Verified Unverified Low confidence (<80%) Link to source
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
CTE vs Temperature(α(T)) | Curve (20 pts) | 1/K | — | — | |
Specific Heat vs Temperature(Cp(T)) | Curve (13 pts) | J/(kg·K) | — | — | |
Thermal Conductivity vs Temperature(k(T)) | Curve (13 pts) | W/(m·K) | — | — |
Rows with are inherited from the base material
Verified Unverified Low confidence (<80%) Link to source
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Density(ρ) | — | kg/m³ | 22°C | — |
Rows with are inherited from the base material
Verified Unverified Low confidence (<80%) Link to source
Regulatory Screening
Environmental
Quality & Standards
Industry-Specific
RoHS, REACH, and Prop 65 statuses are validated against official substance lists (ECHA SVHC Candidate List, OEHHA Prop 65, RoHS Annex II). Other regulations are estimated from composition and material classification. All screening is a starting point for due diligence — always verify with your supplier before making compliance decisions.