AM-355 stainless steel is a martensitic stainless alloy (13% Cr, 4.7% Ni, 2.7% Mo) used in aerospace applications requiring high strength and corrosion resistance at elevated temperatures. The T850 temper (solution heat-treated and age-hardened) provides yield strengths in the 1380–1520 MPa range with good bearing strength and moderate ductility, suitable for critical fasteners, compressor components, and high-stress structural applications to approximately 315°C.
Compliance & Regulations
5 interactive curves for this material
Stress-strain, S-N fatigue and environmental knockdown curves are free with an account.
Create free account| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Ultimate Bearing Strength(Fbru)2 entries | 2.641 | GPa | 22°C · Sheet/Strip · SCT850b · AMS 5547 · t=0.0005-0.187 in · e/D=2 | ||
| ↳ | 2.641 | GPa | 22°C · Plateb · SCT850c · AMS 5549a · t=<0.375 in · e/D=2 | ||
Bearing Yield Strength(Fbry)2 entries | 1.917 | GPa | 22°C · Sheet/Strip · SCT850b · AMS 5547 · t=0.0005-0.187 in · e/D=2 | ||
| ↳ | 1.917 | GPa | 22°C · Plateb · SCT850c · AMS 5549a · t=<0.375 in · e/D=2 | ||
Compressive Modulus(Ec) | 199.9 | GPa | 22°C · Sheet/Strip | ||
Compressive Yield Strength(Fcy)3 entries | 1.241 | GPa | 22°C · Plateb · SCT850c · AMS 5549a · L · t=<0.375 in | ||
| ↳ | 1.241 | GPa | 22°C · Sheet/Strip · SCT850b · AMS 5547 · L · t=0.0005-0.187 in | ||
| ↳ | Curve (13 pts) | Pa | L | ||
Elongation at Break(εf)4 entries | 10.00 | - | 22°C · Bar/Forging · SCT850b · AMS 5743 · L · t=... in | ||
| ↳ | 10.00 | - | 22°C · Plateb · SCT850c · AMS 5549a · LT · t=<0.375 in | ||
| ↳ | 10.00 | - | 22°C · Plateb · SCT850c · AMS 5549a · LT · t=0.375-1.000 in | ||
| ↳ | 10.00 | - | 22°C · Plateb · SCT850c · AMS 5549a · LT · t=>1.000 in | ||
Poisson's Ratio(ν) | 0.3200 | - | 22°C | ||
Reduction of Area(RA) | 20.00 | - | 22°C · Bar/Forging · SCT850b · AMS 5743 · L · t=... in | ||
Shear Modulus(G) | 75.84 | GPa | 22°C · Sheet/Strip | ||
Ultimate Shear Strength(Fsu)3 entries | 854.9 | MPa | 22°C · Plateb · SCT850c · AMS 5549a · t=<0.375 in | ||
| ↳ | 854.9 | MPa | 22°C · Sheet/Strip · SCT850b · AMS 5547 · t=0.0005-0.187 in | ||
| ↳ | Curve (11 pts) | Pa | — | ||
Ultimate Tensile Strength(σUTS) | 1.296 – 1.379 | GPa | 8 entriesClick to expand | ||
Yield Strength (0.2% offset)(σy) | 1.034 – 1.138 | GPa | 7 entriesClick to expand | ||
Young's Modulus(E) | Curve (7 pts) | Pa | L | ||
3 interactive curves for this material
Stress-strain, S-N fatigue and environmental knockdown curves are free with an account.
Create free account| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
CTE vs Temperature(α(T)) | Curve (20 pts) | 1/K | — | ||
Specific Heat vs Temperature(Cp(T)) | Curve (13 pts) | J/(kg·K) | — | ||
Thermal Conductivity vs Temperature(k(T)) | Curve (13 pts) | W/(m·K) | — |
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Density(ρ) | 7.806 | kg/m³ | 22°C |