AM-355 stainless steel is a precipitation-hardenable martensitic stainless steel (17% Cr, 4.3% Ni, 2.6% Mo) used in aerospace fasteners and structural components requiring high strength and corrosion resistance at elevated temperatures. The T1000 condition is aged to approximately 1000°F (538°C), providing ultimate tensile strengths in the range of 180–210 ksi with good fracture toughness and fatigue resistance for service to 600°F (316°C).
Compliance & Regulations
2 interactive curves for this material
Stress-strain, S-N fatigue and environmental knockdown curves are free with an account.
Create free account| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Ultimate Bearing Strength(Fbru) | Curve (10 pts) | Pa | — | ||
Bearing Yield Strength(Fbry) | Curve (12 pts) | Pa | — | ||
Compressive Modulus(Ec) | 199.9 | GPa | 22°C · Sheet/Strip | ||
Elongation at Break(εf)2 entries | 12.00 | - | 22°C · Bar/Forging · SCT1000 · AMS 5743 · L · t=... in | ||
| ↳ | 10.00 | - | 22°C · Sheet/Strip · SCT1000 · AMS 5547 · LT · t=0.010-0.187 in | ||
Poisson's Ratio(ν) | 0.3200 | - | 22°C | ||
Reduction of Area(RA) | 25.00 | - | 22°C · Bar/Forging · SCT1000 · AMS 5743 · L · t=... in | ||
Shear Modulus(G) | 75.84 | GPa | 22°C · Sheet/Strip | ||
Ultimate Tensile Strength(σUTS)2 entries | 1.172 | GPa | 22°C · Bar/Forging · SCT1000 · AMS 5743 · L · t=... in | ||
| ↳ | 1.138 | GPa | 22°C · Sheet/Strip · SCT1000 · AMS 5547 · LT · t=0.010-0.187 in | ||
Yield Strength (0.2% offset)(σy)2 entries | 1.069 | GPa | 22°C · Bar/Forging · SCT1000 · AMS 5743 · L · t=... in | ||
| ↳ | 965.3 | MPa | 22°C · Sheet/Strip · SCT1000 · AMS 5547 · LT · t=0.010-0.187 in | ||
Young's Modulus(E) | 199.9 | GPa | 22°C · Sheet/Strip |
3 interactive curves for this material
Stress-strain, S-N fatigue and environmental knockdown curves are free with an account.
Create free account| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
CTE vs Temperature(α(T)) | Curve (17 pts) | 1/K | — | ||
Specific Heat vs Temperature(Cp(T)) | Curve (13 pts) | J/(kg·K) | — | ||
Thermal Conductivity vs Temperature(k(T)) | Curve (13 pts) | W/(m·K) | — |
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Density(ρ) | 7.806 | kg/m³ | 22°C |