A356.0 is an aluminum-silicon casting alloy (7–8% Si) commonly used in aerospace and automotive applications where lightweight components with good castability and moderate strength are required. The T6 temper (solution heat-treated and artificially aged) provides enhanced strength and hardness suitable for structural and engine components operating at elevated temperatures up to approximately 150°C.
Compliance & Regulations
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Ultimate Bearing Strength(Fbru)2 entries | 448.2 | MPa | 22°C · Casting · T6 · AMS-A-21180 · e/D=1.5 | ||
| ↳ | 558.5 | MPa | 22°C · Casting · T6 · AMS-A-21180 · e/D=2 | ||
Bearing Yield Strength(Fbry)2 entries | 303.4 | MPa | 22°C · Casting · T6 · AMS-A-21180 · e/D=1.5 | ||
| ↳ | 358.5 | MPa | 22°C · Casting · T6 · AMS-A-21180 · e/D=2 | ||
Compressive Modulus(Ec) | 72.39 | GPa | 22°C · Casting | ||
Compressive Yield Strength(Fcy) | 193.1 | MPa | 22°C · Casting · T6 · AMS-A-21180 | ||
Elongation at Break(εf) | 5.000 | - | 22°C · Casting · T6 · AMS-A-21180 | ||
Poisson's Ratio(ν) | 0.3300 | - | 22°C | ||
Shear Modulus(G) | 26.89 | GPa | 22°C · Casting | ||
Ultimate Shear Strength(Fsu) | 165.5 | MPa | 22°C · Casting · T6 · AMS-A-21180 | ||
Ultimate Tensile Strength(σUTS) | 262.0 | MPa | 22°C · Casting · T6 · AMS-A-21180 | ||
Yield Strength (0.2% offset)(σy) | 193.1 | MPa | 22°C · Casting · T6 · AMS-A-21180 | ||
Young's Modulus(E) | 71.71 | GPa | 22°C · Casting |
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Density(ρ) | 2.685 | kg/m³ | 22°C |