7475 aluminum is a zinc-copper-magnesium precipitation-hardened alloy engineered for high-strength aerospace structural applications, particularly where exfoliation corrosion resistance is critical; T651 temper (solution heat-treated, artificially aged, and stress-relieved by controlled stretching) provides ultimate tensile strengths in the 470–510 MPa range with improved through-thickness properties and corrosion resistance compared to T73 variants, making it suitable for highly loaded aircraft components including wing skins, fuselage frames, and pressure vessels.
Compliance & Regulations
6 interactive curves for this material
Stress-strain, S-N fatigue and environmental knockdown curves are free with an account.
Create free account| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Ultimate Bearing Strength(Fbru) | 627.4 – 992.8 | MPa | 6 entriesClick to expand | ||
Bearing Yield Strength(Fbry)3 entries | 730.8 | MPa | 22°C · Plate · T651 · AMS 4090 · t=0.250-0.499 in · e/D=1.5 | ||
| ↳ | 737.7 | MPa | 22°C · Plate · T651 · AMS 4090 · t=0.500-1.000 in · e/D=1.5 | ||
| ↳ | 737.7 | MPa | 22°C · Plate · T651 · AMS 4090 · t=1.001-1.500 in · e/D=1.5 | ||
Compressive Modulus(Ec) | 72.39 | GPa | 22°C · Sheet | ||
Compressive Tangent Modulus vs Stress(Etn(σ))2 entries | Curve (9 pts) | Pa | 21°C · L | ||
| ↳ | Curve (12 pts) | Pa | 21°C · LT | ||
Compressive Yield Strength(Fcy) | 282.7 – 489.5 | MPa | 9 entriesClick to expand | ||
Elongation at Break(εf) | 9.000 – 10.00 | - | 6 entriesClick to expand | ||
Poisson's Ratio(ν) | 0.3300 | - | 22°C | ||
Shear Modulus(G) | 26.20 | GPa | 22°C · Sheet | ||
Ultimate Shear Strength(Fsu)3 entries | 779.1 | MPa | 22°C · Plate · T651 · AMS 4090 · t=0.250-0.499 in | ||
| ↳ | 779.1 | MPa | 22°C · Plate · T651 · AMS 4090 · t=0.500-1.000 in | ||
| ↳ | 779.1 | MPa | 22°C · Plate · T651 · AMS 4090 · t=1.001-1.500 in | ||
Stress–Strain Curve (buckling region, ≤ 2% strain)(σ–ε (low-strain))4 entries | Curve (12 pts) | Pa | 21°C · L | ||
| ↳ | Curve (10 pts) | Pa | 21°C · LT | ||
| ↳ | Curve (6 pts) | Pa | 21°C · L | ||
| ↳ | Curve (8 pts) | Pa | 21°C · LT | ||
Ultimate Tensile Strength(σUTS) | 530.9 – 537.8 | MPa | 6 entriesClick to expand | ||
Yield Strength (0.2% offset)(σy) | 461.9 – 482.6 | MPa | 6 entriesClick to expand | ||
Young's Modulus(E) | 68.95 | GPa | 22°C · Sheet | ||
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Density(ρ) | 2.796 | kg/m³ | 22°C |