7050 Aluminum T7451X is a high-strength Al-Zn-Mg-Cu alloy in an overaged temper condition that combines elevated yield strength (>500 MPa) with improved stress-corrosion cracking (SCC) resistance and fracture toughness suitable for critical aircraft structural applications. The T7451X condition—stress-relieved by stretching and then overaged—provides enhanced resistance to exfoliation corrosion and sustained-load cracking compared to T73, making it preferred for thick-section wing and fuselage components operating in aerospace environments.
Compliance & Regulations
4 interactive curves for this material
Stress-strain, S-N fatigue and environmental knockdown curves are free with an account.
Create free account| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Compressive Modulus(Ec) | 73.08 | GPa | 22°C · Hand Forging | ||
Compressive Tangent Modulus vs Stress(Etn(σ)) | Curve (10 pts) | Pa | 21°C · L | ||
Poisson's Ratio(ν) | 0.3300 | - | 22°C | ||
Shear Modulus(G) | 26.89 | GPa | 22°C · Hand Forging | ||
S–N Curve (Wöhler)(S–N)2 entries | Curve (40 pts) | Pa | 21°C · L | ||
| ↳ | Curve (40 pts) | Pa | 21°C · L | ||
Stress–Strain Curve (buckling region, ≤ 2% strain)(σ–ε (low-strain)) | Curve (7 pts) | Pa | 21°C · L | ||
Young's Modulus(E) | 70.33 | GPa | 22°C · Hand Forging |
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Density(ρ) | 2.823 | kg/m³ | 22°C |