6061 Aluminum T651
VerifiedmetalUNS A96061
6061-T651 is a medium-strength Al-Mg-Si alloy in a solution heat-treated and stress-relieved condition, widely used in aerospace structural applications, marine hardware, and general engineering components where moderate strength and excellent corrosion resistance are required. This temper provides controlled mechanical properties suitable for precision machining with residual stress relief to minimize distortion in service.
aerospacestructural
Compliance & Regulations
?Conflict Free?FDA?RoHS?REACH?TSCA?Prop 65
Filter by
e/D Ratio
Orientation
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Ultimate Bearing Strength(Fbru) | — | Pa | 22°C · Rolled, drawn, or cold-finished rod and special shapes · T651 · AMS 4128 & AMS-QQ-A-225/8 · t=0.500-8.000 in · e/D=1.5 | — | |
Bearing Yield Strength(Fbry)2 entries | — | Pa | 22°C · Rolled, drawn, or cold-finished rod and special shapes · T651 · AMS 4128 & AMS-QQ-A-225/8 · t=0.500-8.000 in · e/D=1.5 | — | |
| ↳ | — | Pa | 22°C · Rolled, drawn, or cold-finished rod and special shapes · T651 · AMS 4128 & AMS-QQ-A-225/8 · t=0.500-8.000 in · e/D=2 | — | |
Compressive Modulus(Ec) | — | Pa | 22°C · Rolled, drawn, or cold-finished rod and special shapes | — | |
Compressive Yield Strength(Fcy)2 entries | — | Pa | 22°C · Rolled, drawn, or cold-finished rod and special shapes · T651 · AMS 4128 & AMS-QQ-A-225/8 · L · t=0.500-8.000 in | — | |
| ↳ | — | Pa | 22°C · Rolled, drawn, or cold-finished rod and special shapes · T651 · AMS 4128 & AMS-QQ-A-225/8 · LT · t=0.500-8.000 in | — | |
Elongation at Break(εf) | — | - | 22°C · Rolled, drawn, or cold-finished rod and special shapes · T651 · AMS 4128 & AMS-QQ-A-225/8 · L · t=0.500-8.000 in | — | |
Poisson's Ratio(ν) | — | - | 22°C | — | |
Shear Modulus(G) | — | Pa | 22°C · Rolled, drawn, or cold-finished rod and special shapes | — | |
Ultimate Shear Strength(Fsu) | — | Pa | 22°C · Rolled, drawn, or cold-finished rod and special shapes · T651 · AMS 4128 & AMS-QQ-A-225/8 · t=0.500-8.000 in | — | |
Stress–Strain Curve(σ–ε)2 entries | Curve (14 pts) | Pa | 21°C · L | — | |
| ↳ | Curve (15 pts) | Pa | 21°C · LT | — | |
Ultimate Tensile Strength(σUTS) | — | Pa | 22°C · Rolled, drawn, or cold-finished rod and special shapes · T651 · AMS 4128 & AMS-QQ-A-225/8 · L · t=0.500-8.000 in | — | |
Yield Strength (0.2% offset)(σy) | — | Pa | 22°C · Rolled, drawn, or cold-finished rod and special shapes · T651 · AMS 4128 & AMS-QQ-A-225/8 · L · t=0.500-8.000 in | — | |
Young's Modulus(E) | — | Pa | 22°C · Rolled, drawn, or cold-finished rod and special shapes | — |
N entriesMultiple entries per property — large groups are collapsed; click a summary row to expand. Use filters above to narrow by form / heat treatment / basis.
Rows with are inherited from the base material
Verified Unverified Low confidence (<80%) Link to source
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
CTE vs Temperature(α(T)) | Curve (11 pts) | 1/K | — | — | |
Specific Heat vs Temperature(Cp(T)) | Curve (17 pts) | J/(kg·K) | — | — |
Rows with are inherited from the base material
Verified Unverified Low confidence (<80%) Link to source
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Density(ρ) | — | kg/m³ | 22°C | — |
Rows with are inherited from the base material
Verified Unverified Low confidence (<80%) Link to source
Regulatory Screening
Environmental
Safety & Biocompatibility
Quality & Standards
Industry-Specific
RoHS, REACH, and Prop 65 statuses are validated against official substance lists (ECHA SVHC Candidate List, OEHHA Prop 65, RoHS Annex II). Other regulations are estimated from composition and material classification. All screening is a starting point for due diligence — always verify with your supplier before making compliance decisions.