6061 Aluminum T62
Verifiedmetal6061-T62 is a heat-treatable aluminum alloy with magnesium and silicon as primary alloying elements, solution heat-treated and artificially aged to T62 condition for moderate strength and good corrosion resistance suitable for aerospace structural components, fasteners, and general engineering applications. This temper provides controlled strength levels with adequate ductility and toughness, commonly supplied as rolled, drawn, or cold-finished rod and special shapes per AMS 4115/4116 specifications.
aerospacestructural
Compliance & Regulations
?Conflict Free?FDA?RoHS?REACH?TSCA?Prop 65
Filter by
Form
Thickness
Orientation
Specification
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Compressive Modulus(Ec) | — | Pa | 22°C · Rolled, drawn, or cold-finished rod and special shapes | — | |
Compressive Tangent Modulus vs Stress(Etn(σ))2 entries | Curve (13 pts) | Pa | 21°C · L | — | |
| ↳ | Curve (12 pts) | Pa | 21°C · LT | — | |
Elongation at Break(εf)2 entries | — | - | 22°C · Rolled, drawn, or cold-finished rod and special shapes · T62a · AMS 4115, AMS 4116, & AMS-QQ-A-225/8 · L · t=≤8.000 in | — | |
| ↳ | — | - | 22°C · Bar/Extrusion/Rod · T62a · AMS 4160 & AMS-QQ-A-200/8 · L · t=All in | — | |
Poisson's Ratio(ν) | — | - | 22°C | — | |
Shear Modulus(G) | — | Pa | 22°C · Rolled, drawn, or cold-finished rod and special shapes | — | |
Stress–Strain Curve(σ–ε)2 entries | Curve (18 pts) | Pa | 21°C · L | — | |
| ↳ | Curve (16 pts) | Pa | 21°C · LT | — | |
Stress–Strain Curve (buckling region, ≤ 2% strain)(σ–ε (low-strain))4 entries | Curve (9 pts) | Pa | 21°C · L | — | |
| ↳ | Curve (10 pts) | Pa | 21°C · L | — | |
| ↳ | Curve (10 pts) | Pa | 21°C · LT | — | |
| ↳ | Curve (7 pts) | Pa | 21°C · LT | — | |
Ultimate Tensile Strength(σUTS)2 entries | — | Pa | 22°C · Rolled, drawn, or cold-finished rod and special shapes · T62a · AMS 4115, AMS 4116, & AMS-QQ-A-225/8 · L · t=≤8.000 in | — | |
| ↳ | — | Pa | 22°C · Bar/Extrusion/Rod · T62a · AMS 4160 & AMS-QQ-A-200/8 · L · t=All in | — | |
Yield Strength (0.2% offset)(σy)2 entries | — | Pa | 22°C · Rolled, drawn, or cold-finished rod and special shapes · T62a · AMS 4115, AMS 4116, & AMS-QQ-A-225/8 · L · t=≤8.000 in | — | |
| ↳ | — | Pa | 22°C · Bar/Extrusion/Rod · T62a · AMS 4160 & AMS-QQ-A-200/8 · L · t=All in | — | |
Young's Modulus(E) | — | Pa | 22°C · Rolled, drawn, or cold-finished rod and special shapes | — |
N entriesMultiple entries per property — large groups are collapsed; click a summary row to expand. Use filters above to narrow by form / heat treatment / basis.
Rows with are inherited from the base material
Verified Unverified Low confidence (<80%) Link to source
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
CTE vs Temperature(α(T)) | Curve (11 pts) | 1/K | — | — | |
Specific Heat vs Temperature(Cp(T)) | Curve (17 pts) | J/(kg·K) | — | — |
Rows with are inherited from the base material
Verified Unverified Low confidence (<80%) Link to source
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Density(ρ) | — | kg/m³ | 22°C | — |
Rows with are inherited from the base material
Verified Unverified Low confidence (<80%) Link to source
Regulatory Screening
Environmental
Safety & Biocompatibility
Quality & Standards
Industry-Specific
RoHS, REACH, and Prop 65 statuses are validated against official substance lists (ECHA SVHC Candidate List, OEHHA Prop 65, RoHS Annex II). Other regulations are estimated from composition and material classification. All screening is a starting point for due diligence — always verify with your supplier before making compliance decisions.