5456 Aluminum H112
Verifiedmetal5456 Aluminum H112 is a 5xxx-series aluminum-magnesium alloy in a strain-hardened and partially annealed condition, offering moderate strength with excellent corrosion resistance in marine and saltwater environments. The H112 temper provides controlled mechanical properties suitable for welded structures and pressure vessels while maintaining good formability and weldability.
aerospacestructural
Compliance & Regulations
?Conflict Free?FDA?RoHS?REACH?TSCA?Prop 65
Property OverviewNormalized to typical max values
Filter by
Form
Thickness
e/D Ratio
Orientation
Specification
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Ultimate Bearing Strength(Fbru)2 entries | 57.00 | ksi | 22°C · Bar/Extrusion/Rod · H112 · AMS-QQ-A-200/7 · t=≤5.000 in · e/D=1.5 | ||
| ↳ | 74.00 | ksi | 22°C · Bar/Extrusion/Rod · H112 · AMS-QQ-A-200/7 · t=≤5.000 in · e/D=2 | ||
Bearing Yield Strength(Fbry)2 entries | 34.00 | ksi | 22°C · Bar/Extrusion/Rod · H112 · AMS-QQ-A-200/7 · t=≤5.000 in · e/D=1.5 | ||
| ↳ | 38.00 | ksi | 22°C · Bar/Extrusion/Rod · H112 · AMS-QQ-A-200/7 · t=≤5.000 in · e/D=2 | ||
Compressive Modulus(Ec) | Curve (19 pts) | ksi | — | ||
Compressive Yield Strength(Fcy)2 entries | 19.00 | ksi | 22°C · Bar/Extrusion/Rod · H112 · AMS-QQ-A-200/7 · L · t=≤5.000 in | ||
| ↳ | 19.00 | ksi | 22°C · Bar/Extrusion/Rod · H112 · AMS-QQ-A-200/7 · LT · t=≤5.000 in | ||
Elongation at Break(εf)3 entries | 12.00 | - | 22°C · Sheet/Plate · H112 · AMS-QQ-A-250/9 · L · t=0.250-1.500 in | ||
| ↳ | 12.00 | - | 22°C · Sheet/Plate · H112 · AMS-QQ-A-250/9 · L · t=1.501-3.000 in | ||
| ↳ | 12.00 | - | 22°C · Bar/Extrusion/Rod · H112 · AMS-QQ-A-200/7 · L · t=≤5.000 in | ||
Poisson's Ratio(ν) | 0.3300 | - | 22°C | ||
Shear Modulus(G) | 3,850 | ksi | 22°C · Sheet/Plate | ||
Ultimate Shear Strength(Fsu) | 23.00 | ksi | 22°C · Bar/Extrusion/Rod · H112 · AMS-QQ-A-200/7 · t=≤5.000 in | ||
Ultimate Tensile Strength(σUTS)4 entries | 42.00 | ksi | 22°C · Sheet/Plate · H112 · AMS-QQ-A-250/9 · L · t=0.250-1.500 in | ||
| ↳ | 41.00 | ksi | 22°C · Sheet/Plate · H112 · AMS-QQ-A-250/9 · L · t=1.501-3.000 in | ||
| ↳ | 41.00 | ksi | 22°C · Bar/Extrusion/Rod · H112 · AMS-QQ-A-200/7 · L · t=≤5.000 in | ||
| ↳ | 41.00 | ksi | 22°C · Bar/Extrusion/Rod · H112 · AMS-QQ-A-200/7 · LT · t=≤5.000 in | ||
Yield Strength (0.2% offset)(σy)4 entries | 19.00 | ksi | 22°C · Sheet/Plate · H112 · AMS-QQ-A-250/9 · L · t=0.250-1.500 in | ||
| ↳ | 18.00 | ksi | 22°C · Sheet/Plate · H112 · AMS-QQ-A-250/9 · L · t=1.501-3.000 in | ||
| ↳ | 19.00 | ksi | 22°C · Bar/Extrusion/Rod · H112 · AMS-QQ-A-200/7 · L · t=≤5.000 in | ||
| ↳ | 19.00 | ksi | 22°C · Bar/Extrusion/Rod · H112 · AMS-QQ-A-200/7 · LT · t=≤5.000 in | ||
Young's Modulus(E) | 10,200 | ksi | 22°C · Sheet/Plate |
N entriesMultiple entries per property — large groups are collapsed; click a summary row to expand. Use filters above to narrow by form / heat treatment / basis.
Rows with are inherited from the base material
Verified Unverified Low confidence (<80%) Link to source
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
CTE vs Temperature(α(T)) | Curve (17 pts) | µin/in·°F | — | ||
Thermal Conductivity vs Temperature(k(T)) | Curve (20 pts) | BTU/(hr·ft·°F) | — |
Rows with are inherited from the base material
Verified Unverified Low confidence (<80%) Link to source
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Density(ρ) | 0.09600 | lb/in³ | 22°C |
Rows with are inherited from the base material
Verified Unverified Low confidence (<80%) Link to source
Regulatory Screening
Environmental
Safety & Biocompatibility
Quality & Standards
RoHS, REACH, and Prop 65 statuses are validated against official substance lists (ECHA SVHC Candidate List, OEHHA Prop 65, RoHS Annex II). Other regulations are estimated from composition and material classification. All screening is a starting point for due diligence — always verify with your supplier before making compliance decisions.