5454 is an aluminum-magnesium alloy (nominally 2.7–3.6% Mg) with excellent corrosion resistance in marine and seawater environments, used in structural applications requiring weldability and moderate strength. The O temper represents the fully annealed condition, providing maximum ductility and formability with reduced strength, suitable for applications requiring cold-working after fabrication or maximum corrosion resistance without strength demands.
Compliance & Regulations
6 interactive curves for this material
Stress-strain, S-N fatigue and environmental knockdown curves are free with an account.
Create free account| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Ultimate Bearing Strength(Fbru)4 entries | 317.2 | MPa | 22°C · Sheet/Plate · O · AMS-QQ-A-250/10 · t=0.020-3.000 in · e/D=1.5 | ||
| ↳ | 330.9 | MPa | 22°C · Sheet/Plate · O · AMS-QQ-A-250/10 · t=0.020-3.000 in · e/D=1.5 | ||
| ↳ | 427.5 | MPa | 22°C · Sheet/Plate · O · AMS-QQ-A-250/10 · t=0.020-3.000 in · e/D=2 | ||
| ↳ | 441.3 | MPa | 22°C · Sheet/Plate · O · AMS-QQ-A-250/10 · t=0.020-3.000 in · e/D=2 | ||
Bearing Yield Strength(Fbry)4 entries | 137.9 | MPa | 22°C · Sheet/Plate · O · AMS-QQ-A-250/10 · t=0.020-3.000 in · e/D=1.5 | ||
| ↳ | 151.7 | MPa | 22°C · Sheet/Plate · O · AMS-QQ-A-250/10 · t=0.020-3.000 in · e/D=1.5 | ||
| ↳ | 165.5 | MPa | 22°C · Sheet/Plate · O · AMS-QQ-A-250/10 · t=0.020-3.000 in · e/D=2 | ||
| ↳ | 179.3 | MPa | 22°C · Sheet/Plate · O · AMS-QQ-A-250/10 · t=0.020-3.000 in · e/D=2 | ||
Compressive Modulus(Ec) | Curve (19 pts) | Pa | — | ||
Compressive Tangent Modulus vs Stress(Etn(σ)) | Curve (12 pts) | Pa | 21°C · LT | ||
Compressive Yield Strength(Fcy) | 82.74 – 89.63 | MPa | 5 entriesClick to expand | ||
Elongation at Break(εf) | 14.00 | - | 22°C · Extrusion · O · AMS-QQ-A-200/6 · L · t=≤5.000a in | ||
Poisson's Ratio(ν) | 0.3300 | - | 22°C | ||
Shear Modulus(G) | 26.54 | GPa | 22°C · Sheet/Plate | ||
Ultimate Shear Strength(Fsu)2 entries | 131.0 | MPa | 22°C · Sheet/Plate · O · AMS-QQ-A-250/10 · t=0.020-3.000 in | ||
| ↳ | 137.9 | MPa | 22°C · Sheet/Plate · O · AMS-QQ-A-250/10 · t=0.020-3.000 in | ||
Stress–Strain Curve (buckling region, ≤ 2% strain)(σ–ε (low-strain))4 entries | Curve (6 pts) | Pa | 21°C · L | ||
| ↳ | Curve (6 pts) | Pa | 21°C · L | ||
| ↳ | Curve (6 pts) | Pa | 21°C · LT | ||
| ↳ | Curve (6 pts) | Pa | 21°C · LT | ||
Ultimate Tensile Strength(σUTS) | 213.7 – 220.6 | MPa | 5 entriesClick to expand | ||
Yield Strength (0.2% offset)(σy) | 82.74 – 89.63 | MPa | 5 entriesClick to expand | ||
Young's Modulus(E) | 70.33 | GPa | 22°C · Sheet/Plate | ||
2 interactive curves for this material
Stress-strain, S-N fatigue and environmental knockdown curves are free with an account.
Create free account| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
CTE vs Temperature(α(T)) | Curve (17 pts) | 1/K | — | ||
Thermal Conductivity vs Temperature(k(T)) | Curve (20 pts) | W/(m·K) | — |
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Density(ρ) | 2.685 | kg/m³ | 22°C |