2618 Aluminum T61
Verifiedmetal2618 aluminum is a copper-aluminum alloy with magnesium and iron additions designed for elevated-temperature aerospace applications, offering strength retention up to 300°C. The T61 temper (solution heat-treated, artificially aged, and stress-relieved) provides optimal combination of tensile strength and thermal stability in die-forged components for aircraft engines and gas turbine applications.
aerospacestructural
Compliance & Regulations
?Conflict Free?FDA?RoHS?REACH?TSCA?Prop 65
Filter by
Thickness
Orientation
Specification
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Ultimate Bearing Strength(Fbru)2 entries | — | Pa | 22°C · Hand forging · T61 · AMS 4132 OR AMS-QQ-A-367 · t=3.001-4.000 in · e/D=2 | — | |
| ↳ | Curve (7 pts) | Pa | — | — | |
Bearing Yield Strength(Fbry)2 entries | — | Pa | 22°C · Hand forging · T61 · AMS 4132 OR AMS-QQ-A-367 · t=3.001-4.000 in · e/D=2 | — | |
| ↳ | Curve (7 pts) | Pa | — | — | |
Compressive Modulus(Ec) | Curve (6 pts) | Pa | L | — | |
Compressive Tangent Modulus vs Stress(Etn(σ)) | Curve (9 pts) | Pa | 21°C · L | — | |
Compressive Yield Strength(Fcy)4 entries | — | Pa | 22°C · Hand forging · T61 · AMS 4132 OR AMS-QQ-A-367 · L · t=3.001-4.000 in | — | |
| ↳ | — | Pa | 22°C · Hand forging · T61 · AMS 4132 OR AMS-QQ-A-367 · LT · t=3.001-4.000 in | — | |
| ↳ | — | Pa | 22°C · Hand forging · T61 · AMS 4132 OR AMS-QQ-A-367 · ST · t=3.001-4.000 in | — | |
| ↳ | Curve (7 pts) | Pa | L | — | |
Elongation at Break(εf) | — | - | 14 entriesClick to expand | ||
Poisson's Ratio(ν) | — | - | 22°C | — | |
Shear Modulus(G) | — | Pa | 22°C · Die forging | — | |
Ultimate Shear Strength(Fsu)2 entries | — | Pa | 22°C · Hand forging · T61 · AMS 4132 OR AMS-QQ-A-367 · t=3.001-4.000 in | — | |
| ↳ | Curve (7 pts) | Pa | — | — | |
Stress–Strain Curve(σ–ε) | Curve (14 pts) | Pa | 21°C · L | — | |
Stress–Strain Curve (buckling region, ≤ 2% strain)(σ–ε (low-strain))2 entries | Curve (12 pts) | Pa | 21°C · L | — | |
| ↳ | Curve (12 pts) | Pa | 21°C · L | — | |
Ultimate Tensile Strength(σUTS) | — | Pa | 16 entriesClick to expand | ||
Yield Strength (0.2% offset)(σy) | — | Pa | 17 entriesClick to expand | ||
Young's Modulus(E) | Curve (7 pts) | Pa | L | — | |
N entriesMultiple entries per property — large groups are collapsed; click a summary row to expand. Use filters above to narrow by form / heat treatment / basis.
Rows with are inherited from the base material
Verified Unverified Low confidence (<80%) Link to source
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
CTE vs Temperature(α(T))2 entries | Curve (8 pts) | 1/K | — | — | |
| ↳ | Curve (8 pts) | 1/K | — | — |
N entriesMultiple entries per property — large groups are collapsed; click a summary row to expand. Use filters above to narrow by form / heat treatment / basis.
Verified Unverified Low confidence (<80%) Link to source
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Density(ρ) | — | kg/m³ | 22°C | — |
Rows with are inherited from the base material
Verified Unverified Low confidence (<80%) Link to source
Regulatory Screening
Environmental
Safety & Biocompatibility
Quality & Standards
RoHS, REACH, and Prop 65 statuses are validated against official substance lists (ECHA SVHC Candidate List, OEHHA Prop 65, RoHS Annex II). Other regulations are estimated from composition and material classification. All screening is a starting point for due diligence — always verify with your supplier before making compliance decisions.