15-5PH Stainless Steel H1100
Verifiedmetal15-5PH Stainless Steel H1100 is a martensitic precipitation-hardening stainless steel (15% Cr, 5% Ni, 3.1% Cu) in the high-strength H1100 condition, providing yield strengths around 1310 MPa with moderate elongation (~8%), used in aerospace fasteners, turbine components, and high-strength applications requiring corrosion resistance to 300°C. The H1100 condition represents full hardening and aging, delivering maximum strength with good fatigue and stress-corrosion cracking resistance compared to lower tempers.
aerospacestructural
Compliance & Regulations
?Conflict Free?RoHS?REACH?TSCA?Prop 65
Filter by
Orientation
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Compressive Modulus(Ec) | — | Pa | 22°C · Bar | — | |
Elongation at Break(εf)2 entries | — | - | 22°C · Bar · H1100 · AMS 5659 · L · t=≤12 in | — | |
| ↳ | — | - | 22°C · Bar · H1100 · AMS 5659 · LT · t=≤12 in | — | |
Poisson's Ratio(ν) | — | - | 22°C | — | |
Reduction of Area(RA)2 entries | — | - | 22°C · Bar · H1100 · AMS 5659 · L · t=≤12 in | — | |
| ↳ | — | - | 22°C · Bar · H1100 · AMS 5659 · LT · t=≤12 in | — | |
Shear Modulus(G) | — | Pa | 22°C · Bar | — | |
Stress–Strain Curve (buckling region, ≤ 2% strain)(σ–ε (low-strain)) | Curve (35 pts) | Pa | 21°C · L | — | |
Ultimate Tensile Strength(σUTS)2 entries | — | Pa | 22°C · Bar · H1100 · AMS 5659 · L · t=≤12 in | — | |
| ↳ | — | Pa | 22°C · Bar · H1100 · AMS 5659 · LT · t=≤12 in | — | |
Yield Strength (0.2% offset)(σy)2 entries | — | Pa | 22°C · Bar · H1100 · AMS 5659 · L · t=≤12 in | — | |
| ↳ | — | Pa | 22°C · Bar · H1100 · AMS 5659 · LT · t=≤12 in | — | |
Young's Modulus(E) | — | Pa | 22°C · Bar | — |
N entriesMultiple entries per property — large groups are collapsed; click a summary row to expand. Use filters above to narrow by form / heat treatment / basis.
Rows with are inherited from the base material
Verified Unverified Low confidence (<80%) Link to source
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
CTE vs Temperature(α(T)) | Curve (11 pts) | 1/K | — | — | |
Thermal Conductivity vs Temperature(k(T)) | Curve (9 pts) | W/(m·K) | — | — |
Rows with are inherited from the base material
Verified Unverified Low confidence (<80%) Link to source
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Density(ρ) | — | kg/m³ | 22°C | — |
Rows with are inherited from the base material
Verified Unverified Low confidence (<80%) Link to source
Regulatory Screening
Environmental
Quality & Standards
Industry-Specific
RoHS, REACH, and Prop 65 statuses are validated against official substance lists (ECHA SVHC Candidate List, OEHHA Prop 65, RoHS Annex II). Other regulations are estimated from composition and material classification. All screening is a starting point for due diligence — always verify with your supplier before making compliance decisions.