SrAlSi is an intermetallic compound combining strontium, aluminum, and silicon, belonging to the family of lightweight metallic materials with potential for structural applications. While not widely commercialized in mainstream engineering, this material represents research interest in the intermetallic alloy space, where the combination of constituent elements offers potential for tailored mechanical properties in niche applications. The material's composition positions it as a candidate for lightweight structural or functional applications where the specific combination of strontium's reactivity, aluminum's light weight, and silicon's hardness characteristics could provide engineering advantages.
Compliance & Regulations
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Bulk Modulus(K)2 entries | 52.29 | GPa | — | ||
| ↳ | 56.83 | GPa | — | ||
Poisson's Ratio(ν) | 0.2000 | - | — | ||
Shear Modulus(G)2 entries | 38.81 | GPa | — | ||
| ↳ | 40.68 | GPa | — |
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Density(ρ) | 3.161 | kg/m³ | — |
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Band Gap(Eg) | 0.00250 range 0.000–0.00500median of 2 measurements | eV | — | ||
Magnetic Moment(μB) | 0.000 | µB | — | ||
Seebeck Coefficient(S) | -10.41 | µV/K | — |
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Energy Above Hull(ΔEhull) | 0.000 | eV/atom | — | ||
Formation Energy(ΔHf) | -0.4818 | eV/atom | — |