PH13-8Mo Stainless Steel H1150
VerifiedmetalPH13-8Mo is a precipitation-hardening martensitic stainless steel (13% Cr, 8% Ni, 2.5% Mo) used in aerospace applications requiring high strength (typically 1300+ MPa yield) combined with moderate corrosion resistance and good fatigue properties; the H1150 condition provides optimal strength through heat treatment at 1150°F with excellent dimensional stability for critical fasteners and structural components.
aerospacestructural
Compliance & Regulations
?Conflict Free?RoHS?REACH?TSCA?Prop 65
Filter by
Form
Thickness
Orientation
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Compressive Modulus(Ec) | — | Pa | 22°C · Round, hex, square and flat bar | — | |
Elongation at Break(εf)4 entries | — | - | 22°C · Round, hex, square and flat bar · H1150 · AMS 5629 · L · t=≤12.0 in | — | |
| ↳ | — | - | 22°C · Extrusion/Forging · H1150 · AMS 5629 · L · t=≤12 in | — | |
| ↳ | — | - | 22°C · Round, hex, square and flat bar · H1150 · AMS 5629 · LT · t=≤12.0 in | — | |
| ↳ | — | - | 22°C · Extrusion/Forging · H1150 · AMS 5629 · LT · t=≤12 in | — | |
Poisson's Ratio(ν) | — | - | 22°C | — | |
Reduction of Area(RA)4 entries | — | - | 22°C · Round, hex, square and flat bar · H1150 · AMS 5629 · L · t=≤12.0 in | — | |
| ↳ | — | - | 22°C · Extrusion/Forging · H1150 · AMS 5629 · L · t=≤12 in | — | |
| ↳ | — | - | 22°C · Round, hex, square and flat bar · H1150 · AMS 5629 · LT · t=≤12.0 in | — | |
| ↳ | — | - | 22°C · Extrusion/Forging · H1150 · AMS 5629 · LT · t=≤12 in | — | |
Shear Modulus(G) | — | Pa | 22°C · Extrusion/Forging | — | |
Ultimate Tensile Strength(σUTS)4 entries | — | Pa | 22°C · Round, hex, square and flat bar · H1150 · AMS 5629 · L · t=≤12.0 in | — | |
| ↳ | — | Pa | 22°C · Extrusion/Forging · H1150 · AMS 5629 · L · t=≤12 in | — | |
| ↳ | — | Pa | 22°C · Round, hex, square and flat bar · H1150 · AMS 5629 · LT · t=≤12.0 in | — | |
| ↳ | — | Pa | 22°C · Extrusion/Forging · H1150 · AMS 5629 · LT · t=≤12 in | — | |
Yield Strength (0.2% offset)(σy)4 entries | — | Pa | 22°C · Round, hex, square and flat bar · H1150 · AMS 5629 · L · t=≤12.0 in | — | |
| ↳ | — | Pa | 22°C · Extrusion/Forging · H1150 · AMS 5629 · L · t=≤12 in | — | |
| ↳ | — | Pa | 22°C · Round, hex, square and flat bar · H1150 · AMS 5629 · LT · t=≤12.0 in | — | |
| ↳ | — | Pa | 22°C · Extrusion/Forging · H1150 · AMS 5629 · LT · t=≤12 in | — | |
Young's Modulus(E) | — | Pa | 22°C · Round, hex, square and flat bar | — |
N entriesMultiple entries per property — large groups are collapsed; click a summary row to expand. Use filters above to narrow by form / heat treatment / basis.
Rows with are inherited from the base material
Verified Unverified Low confidence (<80%) Link to source
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
CTE vs Temperature(α(T)) | Curve (15 pts) | 1/K | — | — | |
Thermal Conductivity vs Temperature(k(T)) | Curve (16 pts) | W/(m·K) | — | — |
Rows with are inherited from the base material
Verified Unverified Low confidence (<80%) Link to source
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Density(ρ) | — | kg/m³ | 22°C | — |
Rows with are inherited from the base material
Verified Unverified Low confidence (<80%) Link to source
Regulatory Screening
Environmental
Quality & Standards
Industry-Specific
RoHS, REACH, and Prop 65 statuses are validated against official substance lists (ECHA SVHC Candidate List, OEHHA Prop 65, RoHS Annex II). Other regulations are estimated from composition and material classification. All screening is a starting point for due diligence — always verify with your supplier before making compliance decisions.