NbSbRu is a ternary intermetallic compound combining niobium, antimony, and ruthenium—an experimental metallic system studied primarily in materials research rather than established in production engineering. This composition falls within the family of refractory and transition-metal intermetallics being investigated for applications requiring high stiffness, thermal stability, and potential corrosion resistance. Research on such ternary systems typically targets next-generation aerospace structures, high-temperature electronics, or catalytic applications where conventional binary alloys reach performance limits.
Compliance & Regulations
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Bulk Modulus(K)3 entries | 168.1 | GPa | — | ||
| ↳ | 168.1 | GPa | — | ||
| ↳ | 169.3 | GPa | — | ||
Elastic Compliance Tensor(Sij) | Matrix (redacted) | 1/GPa | — | ||
Elastic Anisotropy(AU) | 0.000268 | - | — | ||
Elastic Stiffness Tensor(Cij) | Matrix (redacted) | Pa | — | ||
Poisson's Ratio(ν)2 entries | 0.3257 | - | — | ||
| ↳ | 0.3300 | - | — | ||
Shear Modulus(G)3 entries | 66.31 | GPa | — | ||
| ↳ | 66.31 | GPa | — | ||
| ↳ | 63.48 | GPa | — |
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Density(ρ) | 8.779 | kg/m³ | — |
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Band Gap(Eg) | 0.3690 | eV | — | ||
Dielectric Constant (Relative Permittivity)(εr)3 entries | 38.63 | - | — | ||
| ↳ | 39.09 | - | — | ||
| ↳ | 29.84 range 22.60–37.07median of 2 measurements | - | — | ||
Electronic Dielectric Tensor(ε∞) | Matrix (redacted) | - | — | ||
Total Dielectric Tensor(ε) | Matrix (redacted) | - | — | ||
Magnetic Moment(μB) | 0.000 | µB | — | ||
Piezoelectric Modulus(eij)2 entries | 0.8373 | C/m² | — | ||
| ↳ | 0.7289 | C/m² | — | ||
Piezoelectric Stress Tensor(eij) | Matrix (redacted) | C/m² | — | ||
Seebeck Coefficient(S) | -161.2 | µV/K | — |
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Energy Above Hull(ΔEhull) | 0.000 | eV/atom | — | ||
Formation Energy(ΔHf) | -0.3697 | eV/atom | — |