Custom 450 Stainless Steel is a precipitation-hardening martensitic stainless steel (chromium-based with copper and niobium alloying) designed for high-strength aerospace applications requiring corrosion resistance and elevated temperature capability. The H1000 condition represents the highest strength level achievable through precipitation hardening, delivering yield strengths approximately 1700+ MPa with controlled elongation, suitable for critical fasteners and structural components in military and commercial aircraft.
Compliance & Regulations
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Compressive Modulus(Ec) | 213.7 | GPa | 22°C · Bar | ||
Elongation at Break(εf)2 entries | 12.00 | - | 22°C · Bar · H1000 · AMS 5773 · L · t=≤12.000 in | ||
| ↳ | 8.000 | - | 22°C · Bar · H1000 · AMS 5773 · LT · t=≤12.000 in | ||
Poisson's Ratio(ν) | 0.2900 | - | 22°C | ||
Shear Modulus(G) | 77.22 | GPa | 22°C · Bar | ||
Ultimate Tensile Strength(σUTS)2 entries | 1.103 | GPa | 22°C · Bar · H1000 · AMS 5773 · L · t=≤12.000 in | ||
| ↳ | 1.103 | GPa | 22°C · Bar · H1000 · AMS 5773 · LT · t=≤12.000 in | ||
Yield Strength (0.2% offset)(σy)2 entries | 1.034 | GPa | 22°C · Bar · H1000 · AMS 5773 · L · t=≤12.000 in | ||
| ↳ | 1.034 | GPa | 22°C · Bar · H1000 · AMS 5773 · LT · t=≤12.000 in | ||
Young's Modulus(E) | 193.1 | GPa | 22°C · Bar |
1 interactive curve for this material
Stress-strain, S-N fatigue and environmental knockdown curves are free with an account.
Create free account| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
CTE vs Temperature(α(T)) | Curve (16 pts) | 1/K | — |
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Density(ρ) | 7.750 | kg/m³ | 22°C |