Thornel T-300 (Toray) carbon fibre (3,000-filament tow) in an F650 (Hexcel) bismaleimide matrix, supplied as 8-harness satin weave. Carbon/BMI extends carbon/epoxy to sustained service around 350-450 °F, well beyond epoxy's limit, while processing in broadly similar tooling. It is used for engine nacelles and nozzles, structure near exhaust, and supersonic-aircraft skins subject to aerodynamic heating. The handbook characterises it from 75 °F to 450 °F, consistent with elevated-temperature service. MatWorld carries 1 shear curve for this system, digitised from MIL-HDBK-17-2F Volume 2 (US Government work, public domain).
Compliance & Regulations
Fiber Direction
Ply Schedule
Laminate Code
[45/-45/45/-45/45/-45/45/-45/-45/45/-45/45/-45/45/-45/45]s
Fiber angles relative to the 0° reference direction (red arrow in 3D view). 0° = longitudinal, 90° = transverse, ±45° = shear paths.
1 interactive curve for this material
Stress-strain, S-N fatigue and environmental knockdown curves are free with an account.
Create free account| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Interlaminar Shear Strength(ILSS)4 entries | Curve (3 pts) | Pa | RTA · 13-axis · [0:f]:8 · as-measured | ||
| ↳ | 40.20 range 32.75–55.50n=15, 1 batches, CV 15% | MPa | 24°C · RTA · 13-axis · [0:f]:8 · as-measured | ||
| ↳ | 38.54 range 33.99–44.40n=10, 1 batches, CV 10.9% | MPa | 177°C · ETA · 13-axis · [0:f]:8 · as-measured | ||
| ↳ | 39.99 range 36.06–45.30n=10, 1 batches, CV 6.81% | MPa | 232°C · ETA · 13-axis · [0:f]:8 · as-measured | ||
Shear Modulus(G) | 4.757 range 4.068–5.585n=14, 1 batches, CV 10% | GPa | 24°C · RTA · 12-axis · [+-45:f]:4s · as-measured | ||
Ultimate Shear Strength(Fsu) | 67.36 range 59.09–76.53n=15, 1 batches, CV 8.78% | MPa | 24°C · RTA · 12-axis · [+-45:f]:4s · as-measured |