Engineered laminate of AS4/3501-6 unidirectional tape, stacked [0/45/90/-45]:s. Properties here are laminate-level effective values in the laminate's own axes — not the lamina constants, which live on the parent prepreg (AS4/3501-6 unidirectional tape). From MIL-HDBK-17-2F Volume 2 (US Government work, public domain).
Compliance & Regulations
Fiber Direction
Ply Schedule
Laminate Code
[0/45/90/-45/-45/90/45/0]s
Fiber angles relative to the 0° reference direction (red arrow in 3D view). 0° = longitudinal, 90° = transverse, ±45° = shear paths.
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Compressive Modulus(Ec) | 122.7 range 104.1–140.0n=14, 3 batches, CV 7.5% | GPa | 24°C · RTA · 1-axis · [0]:8 · norm. thk+Vf | ||
Compressive Strength(σc) | 289.0 | MPa | T | ||
Interlaminar Shear Strength(ILSS) | 119.3 range 97.22–133.8n=21, 7 batches, CV 7.63% | MPa | 24°C · RTA · 13-axis · [0]:8 · as-measured | ||
Poisson's Ratio(ν) | 0.3000 | - | notes | ||
Shear Modulus(G) | 5.930 | GPa | notes | ||
Ultimate Tensile Strength(σUTS)2 entries | 660.5 range 624.7–730.8n=6, 2 batches, CV 5.95% | MPa | 24°C · RTA · x-axis · [0/45/90/-45]:s · as-measured · rec #1170 | ||
| ↳ | 602.6 range 573.6–639.8n=9, 3 batches, CV 3.43% | MPa | 24°C · RTA · x-axis · [0/45/90/-45]:s · as-measured · rec #1215 | ||
Young's Modulus(E) | 49.78 range 45.51–57.92n=6, 2 batches, CV 9.74% | GPa | 24°C · RTA · x-axis · [0/45/90/-45]:s · as-measured |
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Glass Transition Temperature(Tg) | 473 | K | notes | ||
Thermal Conductivity(k) | 0.6000 | W/(m·K) | T | ||
Coefficient of Thermal Expansion(α (CTE)) | 0.0000250 | 1/K | T |
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Density(ρ) | 1.580 | kg/m³ | — |