AF1410 Steel a
VerifiedmetalAF1410 steel is a low-alloy, case-hardening steel containing nickel, chromium, and molybdenum, specified under AMS 6527 for aerospace bearing and structural applications requiring high compressive strength and fatigue resistance. Condition "a" represents the normalized and tempered state, providing balanced yield and ultimate strengths suitable for bearing races and highly stressed components in aircraft landing gear and power transmission systems.
aerospacestructural
Compliance & Regulations
?Conflict Free?RoHS?REACH?TSCA?Prop 65
Property OverviewNormalized to typical max values
Filter by
e/D Ratio
Orientation
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Ultimate Bearing Strength(Fbru)2 entries | 2.999 | GPa | 22°C · Bar · a · AMS 6527 · e/D=2 | ||
| ↳ | 2.303 | GPa | 22°C · Bar · a · AMS 6527 · e/D=1.5 | ||
Bearing Yield Strength(Fbry)2 entries | 1.855 | GPa | 22°C · Bar · a · AMS 6527 · e/D=1.5 | ||
| ↳ | 2.068 | GPa | 22°C · Bar · a · AMS 6527 · e/D=2 | ||
Compressive Modulus(Ec) | 213.0 | GPa | 22°C · Bar | ||
Compressive Tangent Modulus vs Stress(Etn(σ)) | Curve (12 pts) | Pa | 21°C · L | ||
Compressive Yield Strength(Fcy)2 entries | 1.538 | GPa | 22°C · Bar · a · AMS 6527 · L | ||
| ↳ | 1.551 | GPa | 22°C · Bar · a · AMS 6527 · ST | ||
Elongation at Break(εf)3 entries | 12.00 | - | 22°C · Bar · a · AMS 6527 · L | ||
| ↳ | 12.00 | - | 22°C · Bar · a · AMS 6527 · LT | ||
| ↳ | 12.00 | - | 22°C · Bar · a · AMS 6527 · ST | ||
Reduction of Area(RA)3 entries | 60.00 | - | 22°C · Bar · a · AMS 6527 · L | ||
| ↳ | 55.00 | - | 22°C · Bar · a · AMS 6527 · LT | ||
| ↳ | 55.00 | - | 22°C · Bar · a · AMS 6527 · ST | ||
Ultimate Shear Strength(Fsu) | 972.2 | MPa | 22°C · Bar · a · AMS 6527 | ||
Stress–Strain Curve (buckling region, ≤ 2% strain)(σ–ε (low-strain)) | Curve (6 pts) | Pa | 21°C · L | ||
Ultimate Tensile Strength(σUTS)3 entries | 1.620 | GPa | 22°C · Bar · a · AMS 6527 · L | ||
| ↳ | 1.620 | GPa | 22°C · Bar · a · AMS 6527 · LT | ||
| ↳ | 1.620 | GPa | 22°C · Bar · a · AMS 6527 · ST | ||
Yield Strength (0.2% offset)(σy)3 entries | 1.482 | GPa | 22°C · Bar · a · AMS 6527 · L | ||
| ↳ | 1.482 | GPa | 22°C · Bar · a · AMS 6527 · LT | ||
| ↳ | 1.482 | GPa | 22°C · Bar · a · AMS 6527 · ST | ||
Young's Modulus(E) | 202.7 | GPa | 22°C · Bar |
N entriesMultiple entries per property — large groups are collapsed; click a summary row to expand. Use filters above to narrow by form / heat treatment / basis.
Rows with are inherited from the base material
Verified Unverified Low confidence (<80%) Link to source
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Density(ρ) | 7.833 | kg/m³ | 22°C |
Rows with are inherited from the base material
Verified Unverified Low confidence (<80%) Link to source
Regulatory Screening
Environmental
Quality & Standards
Industry-Specific
RoHS, REACH, and Prop 65 statuses are validated against official substance lists (ECHA SVHC Candidate List, OEHHA Prop 65, RoHS Annex II). Other regulations are estimated from composition and material classification. All screening is a starting point for due diligence — always verify with your supplier before making compliance decisions.