7475 Aluminum T61
Verifiedmetal7475 Aluminum T61 is a high-strength aluminum-zinc-magnesium-copper alloy in an artificially aged condition, providing ultimate tensile strengths in the 500+ MPa range with improved stress-corrosion cracking resistance compared to 7075. Used primarily in aerospace airframe structures and military applications where damage tolerance, fatigue performance, and bearing strength are critical, available as sheet per AMS 4084 specification.
aerospacestructural
Compliance & Regulations
?Conflict Free?FDA?RoHS?REACH?TSCA?Prop 65
Filter by
e/D Ratio
Orientation
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Ultimate Bearing Strength(Fbru)2 entries | — | Pa | 22°C · Sheet · T61 · AMS 4084 · t=0.040-0.249 in · e/D=1.5 | — | |
| ↳ | — | Pa | 22°C · Sheet · T61 · AMS 4084 · t=0.040-0.249 in · e/D=2 | — | |
Bearing Yield Strength(Fbry) | — | Pa | 22°C · Sheet · T61 · AMS 4084 · t=0.040-0.249 in · e/D=1.5 | — | |
Compressive Modulus(Ec) | — | Pa | 22°C · Sheet | — | |
Compressive Tangent Modulus vs Stress(Etn(σ))4 entries | Curve (10 pts) | Pa | 21°C · L | — | |
| ↳ | Curve (11 pts) | Pa | 21°C · LT | — | |
| ↳ | Curve (14 pts) | Pa | 21°C · L | — | |
| ↳ | Curve (15 pts) | Pa | 21°C · LT | — | |
Compressive Yield Strength(Fcy)3 entries | — | Pa | 22°C · Sheet · T61 · AMS 4084 · L · t=0.040-0.249 in | — | |
| ↳ | — | Pa | 22°C · Sheet · T61 · AMS 4084 · LT · t=0.040-0.249 in | — | |
| ↳ | — | Pa | 22°C · Sheet · T61 · AMS 4084 · ST · t=0.040-0.249 in | — | |
Elongation at Break(εf)2 entries | — | - | 22°C · Sheet · T61 · AMS 4084 · L · t=0.040-0.249 in | — | |
| ↳ | — | - | 22°C · Sheet · T61 · AMS 4084 · LT · t=0.040-0.249 in | — | |
Poisson's Ratio(ν) | — | - | 22°C | — | |
Residual Strength vs Initial Crack Length(Fr(2a0))4 entries | Curve (17 pts) | Pa | 21°C | — | |
| ↳ | Curve (17 pts) | Pa | 21°C | — | |
| ↳ | Curve (15 pts) | Pa | 21°C | — | |
| ↳ | Curve (14 pts) | Pa | 21°C | — | |
Shear Modulus(G) | — | Pa | 22°C · Sheet | — | |
Ultimate Shear Strength(Fsu) | — | Pa | 22°C · Sheet · T61 · AMS 4084 · t=0.040-0.249 in | — | |
S–N Curve (Wöhler)(S–N)3 entries | Curve (40 pts) | Pa | 21°C · L | — | |
| ↳ | Curve (40 pts) | Pa | 21°C · L | — | |
| ↳ | Curve (40 pts) | Pa | 21°C · L | — | |
Stress–Strain Curve(σ–ε)2 entries | Curve (15 pts) | Pa | 21°C · L | — | |
| ↳ | Curve (18 pts) | Pa | 21°C · LT | — | |
Stress–Strain Curve (buckling region, ≤ 2% strain)(σ–ε (low-strain)) | — | Pa | 8 entriesClick to expand | ||
Ultimate Tensile Strength(σUTS)2 entries | — | Pa | 22°C · Sheet · T61 · AMS 4084 · L · t=0.040-0.249 in | — | |
| ↳ | — | Pa | 22°C · Sheet · T61 · AMS 4084 · LT · t=0.040-0.249 in | — | |
Yield Strength (0.2% offset)(σy)2 entries | — | Pa | 22°C · Sheet · T61 · AMS 4084 · L · t=0.040-0.249 in | — | |
| ↳ | — | Pa | 22°C · Sheet · T61 · AMS 4084 · LT · t=0.040-0.249 in | — | |
Young's Modulus(E) | — | Pa | 22°C · Sheet | — | |
N entriesMultiple entries per property — large groups are collapsed; click a summary row to expand. Use filters above to narrow by form / heat treatment / basis.
Rows with are inherited from the base material
Verified Unverified Low confidence (<80%) Link to source
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Density(ρ) | — | kg/m³ | 22°C | — |
Rows with are inherited from the base material
Verified Unverified Low confidence (<80%) Link to source
Regulatory Screening
Environmental
Safety & Biocompatibility
Quality & Standards
RoHS, REACH, and Prop 65 statuses are validated against official substance lists (ECHA SVHC Candidate List, OEHHA Prop 65, RoHS Annex II). Other regulations are estimated from composition and material classification. All screening is a starting point for due diligence — always verify with your supplier before making compliance decisions.