7075 Aluminum T73
Verifiedmetal· T7351
7075 aluminum alloy in T73 temper is a high-strength aluminum-zinc-magnesium-copper alloy overaged to improve stress-corrosion cracking resistance while maintaining excellent strength characteristics; it is widely used in aircraft structures, fuselage skins, and aerospace components requiring superior fatigue and corrosion resistance in the 40,000–70,000 psi yield strength range.
aerospacestructural
Compliance & Regulations
?Conflict Free?FDA?RoHS?REACH?TSCA?Prop 65
Filter by
Form
Thickness
e/D Ratio
Orientation
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Ultimate Bearing Strength(Fbru)4 entries | — | Pa | 22°C · Bar/Rod · T73b or T7351 · AMS 4124 OR AMS-QQ-A-225/9 · t=0.375-2.000 in · e/D=1.5 | — | |
| ↳ | — | Pa | 22°C · Bar/Rod · T73b or T7351 · AMS 4124 OR AMS-QQ-A-225/9 · t=2.001-3.000 in · e/D=1.5 | — | |
| ↳ | — | Pa | 22°C · Bar/Rod · T73b or T7351 · AMS 4124 OR AMS-QQ-A-225/9 · t=0.375-2.000 in · e/D=2 | — | |
| ↳ | — | Pa | 22°C · Bar/Rod · T73b or T7351 · AMS 4124 OR AMS-QQ-A-225/9 · t=2.001-3.000 in · e/D=2 | — | |
Bearing Yield Strength(Fbry)4 entries | — | Pa | 22°C · Bar/Rod · T73b or T7351 · AMS 4124 OR AMS-QQ-A-225/9 · t=0.375-2.000 in · e/D=1.5 | — | |
| ↳ | — | Pa | 22°C · Bar/Rod · T73b or T7351 · AMS 4124 OR AMS-QQ-A-225/9 · t=2.001-3.000 in · e/D=1.5 | — | |
| ↳ | — | Pa | 22°C · Bar/Rod · T73b or T7351 · AMS 4124 OR AMS-QQ-A-225/9 · t=0.375-2.000 in · e/D=2 | — | |
| ↳ | — | Pa | 22°C · Bar/Rod · T73b or T7351 · AMS 4124 OR AMS-QQ-A-225/9 · t=2.001-3.000 in · e/D=2 | — | |
Compressive Modulus(Ec) | — | Pa | 22°C · Bar/Rod | — | |
Compressive Tangent Modulus vs Stress(Etn(σ))2 entries | Curve (13 pts) | Pa | 21°C · L | — | |
| ↳ | Curve (13 pts) | Pa | 21°C · LT | — | |
Compressive Yield Strength(Fcy)3 entries | — | Pa | 22°C · Bar/Rod · T73b or T7351 · AMS 4124 OR AMS-QQ-A-225/9 · L · t=0.375-2.000 in | — | |
| ↳ | — | Pa | 22°C · Bar/Rod · T73b or T7351 · AMS 4124 OR AMS-QQ-A-225/9 · L · t=2.001-3.000 in | — | |
| ↳ | — | Pa | 22°C · Bar/Rod · T73b or T7351 · AMS 4124 OR AMS-QQ-A-225/9 · LT · t=2.001-3.000 in | — | |
Elongation at Break(εf)2 entries | — | - | 22°C · Bar/Rod · T73b or T7351 · AMS 4124 OR AMS-QQ-A-225/9 · L · t=0.375-2.000 in | — | |
| ↳ | — | - | 22°C · Bar/Rod · T73b or T7351 · AMS 4124 OR AMS-QQ-A-225/9 · L · t=2.001-3.000 in | — | |
Poisson's Ratio(ν) | — | - | 22°C | — | |
Shear Modulus(G) | — | Pa | 22°C · Bar/Rod | — | |
Ultimate Shear Strength(Fsu)2 entries | — | Pa | 22°C · Bar/Rod · T73b or T7351 · AMS 4124 OR AMS-QQ-A-225/9 · t=0.375-2.000 in | — | |
| ↳ | — | Pa | 22°C · Bar/Rod · T73b or T7351 · AMS 4124 OR AMS-QQ-A-225/9 · t=2.001-3.000 in | — | |
Stress–Strain Curve(σ–ε)2 entries | Curve (17 pts) | Pa | 21°C · L | — | |
| ↳ | Curve (13 pts) | Pa | 21°C · LT | — | |
Stress–Strain Curve (buckling region, ≤ 2% strain)(σ–ε (low-strain))4 entries | Curve (9 pts) | Pa | 21°C · L | — | |
| ↳ | Curve (9 pts) | Pa | 21°C · L | — | |
| ↳ | Curve (9 pts) | Pa | 21°C · LT | — | |
| ↳ | Curve (6 pts) | Pa | 21°C · LT | — | |
Ultimate Tensile Strength(σUTS)3 entries | — | Pa | 22°C · Bar/Rod · T73b or T7351 · AMS 4124 OR AMS-QQ-A-225/9 · L · t=0.375-2.000 in | — | |
| ↳ | — | Pa | 22°C · Bar/Rod · T73b or T7351 · AMS 4124 OR AMS-QQ-A-225/9 · L · t=2.001-3.000 in | — | |
| ↳ | — | Pa | 22°C · Bar/Rod · T73b or T7351 · AMS 4124 OR AMS-QQ-A-225/9 · LT · t=2.001-3.000 in | — | |
Yield Strength (0.2% offset)(σy)3 entries | — | Pa | 22°C · Bar/Rod · T73b or T7351 · AMS 4124 OR AMS-QQ-A-225/9 · L · t=0.375-2.000 in | — | |
| ↳ | — | Pa | 22°C · Bar/Rod · T73b or T7351 · AMS 4124 OR AMS-QQ-A-225/9 · L · t=2.001-3.000 in | — | |
| ↳ | — | Pa | 22°C · Bar/Rod · T73b or T7351 · AMS 4124 OR AMS-QQ-A-225/9 · LT · t=2.001-3.000 in | — | |
Young's Modulus(E) | — | Pa | 22°C · Bar/Rod | — |
N entriesMultiple entries per property — large groups are collapsed; click a summary row to expand. Use filters above to narrow by form / heat treatment / basis.
Rows with are inherited from the base material
Verified Unverified Low confidence (<80%) Link to source
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
CTE vs Temperature(α(T)) | Curve (5 pts) | 1/K | — | — | |
Specific Heat vs Temperature(Cp(T)) | Curve (5 pts) | J/(kg·K) | — | — | |
Thermal Conductivity vs Temperature(k(T)) | Curve (4 pts) | W/(m·K) | — | — |
Rows with are inherited from the base material
Verified Unverified Low confidence (<80%) Link to source
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Density(ρ) | — | kg/m³ | 22°C | — |
Rows with are inherited from the base material
Verified Unverified Low confidence (<80%) Link to source
Regulatory Screening
Environmental
Safety & Biocompatibility
Quality & Standards
RoHS, REACH, and Prop 65 statuses are validated against official substance lists (ECHA SVHC Candidate List, OEHHA Prop 65, RoHS Annex II). Other regulations are estimated from composition and material classification. All screening is a starting point for due diligence — always verify with your supplier before making compliance decisions.