6061 Aluminum T4
VerifiedmetalUNS A96061
6061-T4 is a precipitation-hardenable aluminum alloy (Al-Mg-Si system) in solution heat-treated and naturally aged condition, offering moderate strength with good corrosion resistance and weldability for aerospace structures, aircraft components, and general engineering applications. The T4 temper provides lower strength than T6 but superior ductility and machinability, making it suitable for applications requiring formability and toughness after solution treatment.
aerospacestructural
Compliance & Regulations
?Conflict Free?FDA?RoHS?REACH?TSCA?Prop 65
Filter by
Form
Heat Treatment
Thickness
e/D Ratio
Orientation
Specification
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Ultimate Bearing Strength(Fbru)3 entries | — | Pa | 22°C · Rolled, drawn, or cold-finished rod and special shapes · T4 · AMS 4116 & AMS-QQ-A-225/8 · t=≤8.000 in · e/D=1.5 | — | |
| ↳ | — | Pa | 22°C · Bar/Extrusion/Rod · T4, T4510, and T4511 · AMS 4161, AMS 4172, & AMS-QQ-A-200/8 · t=≤3.000 in · e/D=1.5 | — | |
| ↳ | — | Pa | 22°C · Bar/Extrusion/Rod · T4, T4510, and T4511 · AMS 4161, AMS 4172, & AMS-QQ-A-200/8 · t=≤3.000 in · e/D=2 | — | |
Bearing Yield Strength(Fbry)4 entries | — | Pa | 22°C · Rolled, drawn, or cold-finished rod and special shapes · T4 · AMS 4116 & AMS-QQ-A-225/8 · t=≤8.000 in · e/D=1.5 | — | |
| ↳ | — | Pa | 22°C · Rolled, drawn, or cold-finished rod and special shapes · T4 · AMS 4116 & AMS-QQ-A-225/8 · t=≤8.000 in · e/D=2 | — | |
| ↳ | — | Pa | 22°C · Bar/Extrusion/Rod · T4, T4510, and T4511 · AMS 4161, AMS 4172, & AMS-QQ-A-200/8 · t=≤3.000 in · e/D=1.5 | — | |
| ↳ | — | Pa | 22°C · Bar/Extrusion/Rod · T4, T4510, and T4511 · AMS 4161, AMS 4172, & AMS-QQ-A-200/8 · t=≤3.000 in · e/D=2 | — | |
Compressive Modulus(Ec) | — | Pa | 22°C · Rolled, drawn, or cold-finished rod and special shapes | — | |
Compressive Yield Strength(Fcy)3 entries | — | Pa | 22°C · Rolled, drawn, or cold-finished rod and special shapes · T4 · AMS 4116 & AMS-QQ-A-225/8 · L · t=≤8.000 in | — | |
| ↳ | — | Pa | 22°C · Rolled, drawn, or cold-finished rod and special shapes · T4 · AMS 4116 & AMS-QQ-A-225/8 · LT · t=≤8.000 in | — | |
| ↳ | — | Pa | 22°C · Bar/Extrusion/Rod · T4, T4510, and T4511 · AMS 4161, AMS 4172, & AMS-QQ-A-200/8 · L · t=≤3.000 in | — | |
Elongation at Break(εf)2 entries | — | - | 22°C · Rolled, drawn, or cold-finished rod and special shapes · T4 · AMS 4116 & AMS-QQ-A-225/8 · L · t=≤8.000 in | — | |
| ↳ | — | - | 22°C · Bar/Extrusion/Rod · T4, T4510, and T4511 · AMS 4161, AMS 4172, & AMS-QQ-A-200/8 · L · t=≤3.000 in | — | |
Poisson's Ratio(ν) | — | - | 22°C | — | |
Shear Modulus(G) | — | Pa | 22°C · Rolled, drawn, or cold-finished rod and special shapes | — | |
Ultimate Shear Strength(Fsu)2 entries | — | Pa | 22°C · Rolled, drawn, or cold-finished rod and special shapes · T4 · AMS 4116 & AMS-QQ-A-225/8 · t=≤8.000 in | — | |
| ↳ | — | Pa | 22°C · Bar/Extrusion/Rod · T4, T4510, and T4511 · AMS 4161, AMS 4172, & AMS-QQ-A-200/8 · t=≤3.000 in | — | |
Ultimate Tensile Strength(σUTS)2 entries | — | Pa | 22°C · Rolled, drawn, or cold-finished rod and special shapes · T4 · AMS 4116 & AMS-QQ-A-225/8 · L · t=≤8.000 in | — | |
| ↳ | — | Pa | 22°C · Bar/Extrusion/Rod · T4, T4510, and T4511 · AMS 4161, AMS 4172, & AMS-QQ-A-200/8 · L · t=≤3.000 in | — | |
Yield Strength (0.2% offset)(σy)2 entries | — | Pa | 22°C · Rolled, drawn, or cold-finished rod and special shapes · T4 · AMS 4116 & AMS-QQ-A-225/8 · L · t=≤8.000 in | — | |
| ↳ | — | Pa | 22°C · Bar/Extrusion/Rod · T4, T4510, and T4511 · AMS 4161, AMS 4172, & AMS-QQ-A-200/8 · L · t=≤3.000 in | — | |
Young's Modulus(E) | — | Pa | 22°C · Rolled, drawn, or cold-finished rod and special shapes | — |
N entriesMultiple entries per property — large groups are collapsed; click a summary row to expand. Use filters above to narrow by form / heat treatment / basis.
Rows with are inherited from the base material
Verified Unverified Low confidence (<80%) Link to source
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
CTE vs Temperature(α(T)) | Curve (11 pts) | 1/K | — | — | |
Specific Heat vs Temperature(Cp(T)) | Curve (17 pts) | J/(kg·K) | — | — |
Rows with are inherited from the base material
Verified Unverified Low confidence (<80%) Link to source
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Density(ρ) | — | kg/m³ | 22°C | — |
Rows with are inherited from the base material
Verified Unverified Low confidence (<80%) Link to source
Regulatory Screening
Environmental
Safety & Biocompatibility
Quality & Standards
Industry-Specific
RoHS, REACH, and Prop 65 statuses are validated against official substance lists (ECHA SVHC Candidate List, OEHHA Prop 65, RoHS Annex II). Other regulations are estimated from composition and material classification. All screening is a starting point for due diligence — always verify with your supplier before making compliance decisions.