17-4PH stainless steel is a precipitation-hardening martensitic stainless steel (Fe-Cr-Ni-Cu-Nb) offering high strength and corrosion resistance, widely used in aerospace and defense applications including fasteners, shafts, and structural components. The H1150Ma condition is solution-annealed at 1150°F and aged to provide optimized strength-ductility balance with good fracture toughness for critical forged, tubed, and ring components per AMS 5643.
Compliance & Regulations
1 interactive curve for this material
Stress-strain, S-N fatigue and environmental knockdown curves are free with an account.
Create free account| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Compressive Modulus(Ec) | Curve (10 pts) | Pa | — | ||
Elongation at Break(εf) | 18.00 | - | 22°C · Forging/Tubing · H1150Ma · AMS 5643 · L · t=<8.000 in | ||
Poisson's Ratio(ν) | 0.2700 | - | 22°C | ||
Shear Modulus(G) | 87.56 | GPa | 22°C · Investment Casting | ||
Ultimate Tensile Strength(σUTS) | 792.9 | MPa | 22°C · Forging/Tubing · H1150Ma · AMS 5643 · L · t=<8.000 in | ||
Yield Strength (0.2% offset)(σy) | 517.1 | MPa | 22°C · Forging/Tubing · H1150Ma · AMS 5643 · L · t=<8.000 in | ||
Young's Modulus(E) | 196.5 | GPa | 22°C · Sheet/Strip/Plate |
3 interactive curves for this material
Stress-strain, S-N fatigue and environmental knockdown curves are free with an account.
Create free account| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
CTE vs Temperature(α(T)) | Curve (13 pts) | 1/K | — | ||
Specific Heat vs Temperature(Cp(T)) | Curve (17 pts) | J/(kg·K) | — | ||
Thermal Conductivity vs Temperature(k(T)) | Curve (17 pts) | W/(m·K) | — |
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Density(ρ) | 7.806 | kg/m³ | 22°C |