17-4PH Stainless Steel H1100
Verifiedmetal17-4PH (precipitation-hardened stainless steel) in H1100 condition is a martensitic stainless steel strengthened by copper and niobium precipitation, offering yield strength around 1,310 MPa with good corrosion resistance and toughness, used extensively in aerospace applications including fasteners, shafts, and structural components. The H1100 temper provides a balance of high strength and ductility through controlled aging after solution treatment and cold work.
aerospacestructural
Compliance & Regulations
?Conflict Free?RoHS?REACH?TSCA?Prop 65
Filter by
Form
Heat Treatment
Thickness
e/D Ratio
Basis
Orientation
Specification
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Ultimate Bearing Strength(Fbru)4 entries | — | Pa | 22°C · Bar · H1100 · AMS 5643 · t=<8.000 in · e/D=1.5 | — | |
| ↳ | — | Pa | 22°C · Bar · H1100 · AMS 5643 · t=<8.000 in · e/D=1.5 | — | |
| ↳ | — | Pa | 22°C · Bar · H1100 · AMS 5643 · t=<8.000 in · e/D=2 | — | |
| ↳ | — | Pa | 22°C · Bar · H1100 · AMS 5643 · t=<8.000 in · e/D=2 | — | |
Bearing Yield Strength(Fbry)4 entries | — | Pa | 22°C · Bar · H1100 · AMS 5643 · t=<8.000 in · e/D=1.5 | — | |
| ↳ | — | Pa | 22°C · Bar · H1100 · AMS 5643 · t=<8.000 in · e/D=1.5 | — | |
| ↳ | — | Pa | 22°C · Bar · H1100 · AMS 5643 · t=<8.000 in · e/D=2 | — | |
| ↳ | — | Pa | 22°C · Bar · H1100 · AMS 5643 · t=<8.000 in · e/D=2 | — | |
Compressive Modulus(Ec) | Curve (10 pts) | Pa | — | — | |
Compressive Yield Strength(Fcy)2 entries | — | Pa | 22°C · Bar · H1100 · AMS 5643 · L · t=<8.000 in | — | |
| ↳ | — | Pa | 22°C · Bar · H1100 · AMS 5643 · L · t=<8.000 in | — | |
Elongation at Break(εf)3 entries | — | - | 22°C · Forging/Tubing · H1100 · AMS 5643 · L · t=<8.000 in | — | |
| ↳ | — | - | 22°C · Bar · H1100 · AMS 5643 · L · t=<8.000 in | — | |
| ↳ | — | - | 22°C · Investment Casting · H1100c · AMS 5342 | — | |
Poisson's Ratio(ν) | — | - | 22°C | — | |
Reduction of Area(RA) | — | - | 22°C · Investment Casting · H1100c · AMS 5342 | — | |
Shear Modulus(G) | — | Pa | 22°C · Investment Casting | — | |
Ultimate Shear Strength(Fsu)2 entries | — | Pa | 22°C · Bar · H1100 · AMS 5643 · t=<8.000 in | — | |
| ↳ | — | Pa | 22°C · Bar · H1100 · AMS 5643 · t=<8.000 in | — | |
S–N Curve (Wöhler)(S–N)4 entries | Curve (40 pts) | Pa | 21°C · L | — | |
| ↳ | Curve (40 pts) | Pa | 21°C · L | — | |
| ↳ | Curve (5 pts) | Pa | 21°C · L | — | |
| ↳ | Curve (5 pts) | Pa | 21°C · L | — | |
Ultimate Tensile Strength(σUTS) | — | Pa | 5 entriesClick to expand | ||
Yield Strength (0.2% offset)(σy) | — | Pa | 5 entriesClick to expand | ||
Young's Modulus(E) | — | Pa | 22°C · Sheet/Strip/Plate | — | |
N entriesMultiple entries per property — large groups are collapsed; click a summary row to expand. Use filters above to narrow by form / heat treatment / basis.
Rows with are inherited from the base material
Verified Unverified Low confidence (<80%) Link to source
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
CTE vs Temperature(α(T)) | Curve (13 pts) | 1/K | — | — | |
Specific Heat vs Temperature(Cp(T)) | Curve (17 pts) | J/(kg·K) | — | — | |
Thermal Conductivity vs Temperature(k(T)) | Curve (17 pts) | W/(m·K) | — | — |
Rows with are inherited from the base material
Verified Unverified Low confidence (<80%) Link to source
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Density(ρ) | — | kg/m³ | 22°C | — |
Rows with are inherited from the base material
Verified Unverified Low confidence (<80%) Link to source
Regulatory Screening
Environmental
Quality & Standards
Industry-Specific
RoHS, REACH, and Prop 65 statuses are validated against official substance lists (ECHA SVHC Candidate List, OEHHA Prop 65, RoHS Annex II). Other regulations are estimated from composition and material classification. All screening is a starting point for due diligence — always verify with your supplier before making compliance decisions.